| About |
|---|
| Product Description | |
|---|---|
| Supplier | Evonik |
| Generic | PA Not specified |
| Material Status | Commercial: Active |
| Availabilitys | Europe |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| Tensile modulus | 1480 / 1490 | MPa | ISO 527 |
| tensile strength | 59 / 63 | MPa | ISO 527 |
| Yield stress | 59 / 63 | MPa | ISO 527 |
| Yield strain | 8 / 7 | % | ISO 527 |
| Stress at 50% strain | 42 / 39 | MPa | ISO 527 |
| Fracture stress | 65 / 60 | MPa | ISO 527 |
| The nominal strain at fracture, ε TB | >50 / >50 | % | ISO 527 |
| Bending modulus, 23 ° C | 1460 / 1500 | MPa | ISO 178 |
| Bending stress during deflection conversion at 23 ° C | 52 / 54 | MPa | ISO 178 |
| Bending strain under bending strength, 23 ° C | 8 / 8 | % | ISO 178 |
| Bending stress at fracture, 23 ° C | N / N | MPa | ISO 178 |
| Bending strain at fracture, 23 ° C | N / N | % | ISO 178 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | 247 | °C | ISO 11357-1/-3 |
| Glass transition temperature | 135 | °C | ISO 11357-1/-2 |
| Hot deformation temperature | |||
| 1.80 MPa | 102 | °C | ISO 75-1/-2 |
| 0.45 MPa | 120 | °C | ISO 75-1/-2 |
| Vicat Softening Temp | |||
| 10 N, 50 K/h | 133 | °C | ISO 306 |
| 50 N，50 K/h | 127 | °C | ISO 306 |
| Linear coefficient of thermal expansion | |||
| parallel | 92 | E-6/K | ISO 11359-1/-2 |
| normal | 96 | E-6/K | ISO 11359-1/-2 |
| Melting temperature | 247 | °C | ASTM D 3418 |
| physical characteristics | Nominal value | Unit | Test method |
|---|---|---|---|
| Water absorption rate | 3 | % | Sim. to ISO 62 |
| Hygroscopicity | 2 | % | Sim. to ISO 62 |
| dense | 1020 | kg/m³ | ISO 1183 |
| Shaw D hardness | 81[b] | – | ISO 7619-1 |
| dense | 1020 | kg/m³ | ASTM D 792 |
| optical characteristics | Nominal value | Unit | Test method |
|---|---|---|---|
| mist | 2.1 | % | ASTM D 1003 |
| Test fog layer thickness | 2 | mm | – |
| Transmittance | 92 | % | ASTM D 1003 |
| Test transmittance thickness | 2 | mm | ASTM D 1003 |
| Rheological properties | Nominal value | Unit | Test method |
|---|---|---|---|
| Melt Volume Rate | 10.5 | cm³/10min | ISO 1133 |
| temperature | 280 | °C | – |
| load | 2.16 | kg | – |
| Forming shrinkage, parallel | 0.7 | % | ISO 294-4, 2577 |
| Forming shrinkage, normal | 0.7 | % | ISO 294-4, 2577 |
| Mold temperature | 80 | °C | – |
| Melt Temperature | 280 | °C | – |
| Flow length | 295 | mm | Evonik standard |
| Flow cross-section | 6 x 2 | mm² | Evonik standard |
| Mold temperature, flow spiral | 80 | °C | Evonik standard |
| Melt temperature, flow spiral | 280 | °C | Evonik standard |
| Jet pressure, flow spiral | 1000 | bar | Evonik standard |
| Flow length | 464 | mm | Evonik standard |
| Flow cross-section | 6 x 2 | mm² | Evonik standard |
| Mold temperature, flow spiral | 80 | °C | Evonik standard |
| Melt temperature, flow spiral | 300 | °C | Evonik standard |
| Jet pressure, flow spiral | 1000 | bar | Evonik standard |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy impact strength | |||
| 23°C | N / N | KJ/㎡ | ISO 179/1eU |
| -30°C | N / N | KJ/㎡ | ISO 179/1eU |
| Charpy Notched Impact Strength | |||
| 23°C | 11 / 12 | KJ/㎡ | ISO 179/1eA |
| -30°C | 11 / 12 | KJ/㎡ | ISO 179/1eA |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |