| About |
|---|
| TRYCITE™ 8003 Polystyrene Film is a matte finish, translucent, oriented polystyrene film for use in lamination applications. Available thicknesses of 1.0, 1.15, 1.25, 1.5, 2.0, 2.5, and 3.0 mil.&& |
| Product Description | |
|---|---|
| Supplier | DOW |
| Generic | PS (HIPS) |
| Material Status | Commercial: Active |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| film | Nominal value | Unit | Test method |
| film thickness | 1.0; 1.15; 1.25; 1.5; 2.0; 2.5; 3.0 mil (25; 29; 32; 38; 51; 64; 76 µ | ||
| Secant modulus | ASTM D882 | ||
| 1% secant, MD | 2480 | MPa | ASTM D882 |
| 1% secant, TD | 2550 | MPa | ASTM D882 |
| tensile strength | ASTM D882 | ||
| MD, yield | 55.8 | MPa | ASTM D882 |
| TD, yield | 55.8 | MPa | ASTM D882 |
| Tensile strain | ASTM D882 | ||
| MD, fracture | 70 | % | ASTM D882 |
| TD, fracture | 90 | % | ASTM D882 |
| Drop hammer impact | 200 | g | ASTM D1709 |
| Elmandorf tear strength | |||
| TD，25 µm | 7.0 | g | ASTM D1922 |
| Shrinkage and stretching | Internal Method | ||
| MD：135℃ | 1.21 | MPa | Internal Method |
| TD：135℃ | 0.896 | MPa | Internal Method |
| dosage | ASTM D4321 | ||
| 25.4 µm | 38.0 | m²/kg | ASTM D4321 |
| 29.2 µm | 33.0 | m²/kg | ASTM D4321 |
| 31.8 µm | 30.0 | m²/kg | ASTM D4321 |
| 38.1 µm | 25.0 | m²/kg | ASTM D4321 |
| 50.8 µm | 18.9 | m²/kg | ASTM D4321 |
| 63.5 µm | 15.2 | m²/kg | ASTM D4321 |
| 76.2 µm | 12.6 | m²/kg | ASTM D4321 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 60° | 20 | ASTM D2457 | |
| Haze | 56 | % | ASTM D1003 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |