| About |
|---|
| Common Features of Tufnyl® Nylon resin include excellent mechanical and physical properties such as high mechanical strength, excellent balance of stiffness and toughness, good high temperature performance, good electrical properties, abrasion and chemical resistance. Nylon 6 Glass Filled material for Injection Molding.&& |
| Product Description | |
|---|---|
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | HB |
| Availabilitys | Africa & Middle East ,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.20 | g/cm³ | ISO 1183 |
| Shrinkage rate | ISO 294-4 | ||
| TD | 0.60 to 0.90 | % | ISO 294-4 |
| MD | 0.70 to 1.1 | % | ISO 294-4 |
| water content | < 0.20 | % | |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 7.0 | kJ/m² | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 170 | ℃ | ISO 75-2/A |
| Melting temperature | 220 | ℃ | ISO 11357-3 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+12 | ohms | ASTM D257 |
| Volume resistivity | 1.0E+13 | ohms·cm | ASTM D257 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 3.00 mm | HB | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | ISO 2039-2 | ||
| M-level | 75 | ISO 2039-2 | |
| R-level | 112 | ISO 2039-2 | |
| tensile strength | |||
| fracture | 77.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 3.5 | % | ISO 527-2 |
| Bending modulus | 3000 | MPa | ISO 178 |
| bending strength | 130 | MPa | ISO 178 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | |||
| Desiccant desiccant | 80 | °C | |
| Vacuum dryer | 100 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Barrel rear temperature | 260 to 265 | °C | |
| Barrel middle temperature | 265 to 270 | °C | |
| Barrel front temperature | 270 to 275 | °C | |
| Nozzle temperature | 265 to 275 | °C | |
| Mold temperature | 80 to 100 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |