| Polyamide 6, Un-filled, red pigmented material for injection molding&& |
| Product Description | |
|---|---|
| Generic | PA6 |
| Material Status | Commercial: Active |
| Availabilitys | Africa & Middle East ,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.13 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD | 1.5 to 1.7 | % | Internal Method |
| Water absorption rate | |||
| balance | 2.0 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | 49.0 | J/m | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 140 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed | 70.0 | ℃ | ISO 75-2/A |
| Melting temperature | 220 | ℃ | DSC |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+14 | ohms | ASTM D257 |
| Volume resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric strength | 21 | kV/mm | ASTM D149 |
| Compared to the leakage tracing index | > 600 | V | IEC 60112 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | ASTM D785 | ||
| M-level | 75 | ASTM D785 | |
| R-level | 115 | ASTM D785 | |
| tensile strength | |||
| yield | 65.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 15 | % | ISO 527-2 |
| Bending modulus | 2500 | MPa | ISO 178 |
| bending strength | 110 | MPa | ISO 178 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Recommended maximum moisture content | < 0.20 | % | |
| Processing (melt) temperature | 280 to 300 | °C | |
| Mold temperature | 40 to 80 | °C | |
| Injection pressure | 3.50 to 12.5 | MPa | |
| Injection speed | 快速 | ||
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |