| About |
|---|
| Common Features of TUFPC® Polycabonate Compounds include excellent mechanical and physical properties such as high mechanical strength, excellent balance of stiffness and toughness, good high temperature performance, good electrical properties, abrasion and chemical resistance. Polycarbonate Unfilled material for Injection Molding.&& |
| Product Description | |
|---|---|
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good Electrical Properties,Good wear resistance,Heat Resistance, Good,Solvent resistance |
| Availabilitys | Africa & Middle East ,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.20 | g/cm³ | ISO 1183 |
| water content | < 0.080 | % | |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 70 | kJ/m² | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 120 | ℃ | ISO 75-2/A |
| Melting temperature | |||
| DSC | 265 | ℃ | ISO 3146 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+12 | ohms | ASTM D257 |
| Volume resistivity | 1.0E+12 | ohms·cm | ASTM D257 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| M-level | 70 | ||
| R-level | 115 | ||
| tensile strength | |||
| fracture | 60.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 25 | % | ISO 527-2 |
| Bending modulus | 2500 | MPa | ISO 178 |
| bending strength | 100 | MPa | ISO 178 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | |||
| Desiccant desiccant | 80 | °C | |
| Vacuum dryer | 100 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Barrel rear temperature | 255 to 265 | °C | |
| Barrel middle temperature | 270 to 280 | °C | |
| Barrel front temperature | 280 to 290 | °C | |
| Nozzle temperature | 275 to 285 | °C | |
| Mold temperature | 80 to 100 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |