| About |
|---|
| TYRIL* styrene-acrylonitrile (SAN) resins are designed to offer superior chemical resistance, strength, hardness and dimensional stability in a broad range of product applications. The key property of TYRIL 867 is excellent balance of physical properties. TYRIL 867 E is specifically designed to provide good processability, good chemical and heat resistance and very good strength. The UV-stabilized version exhibits excellent weather ability, suitable in particular for extruded sheet and thermoforming applications. Applications: Small appliances: transparent kitchen-robot parts Extruded sheet for shower cabinets, light-diffusers Housewares: food storage containers Sanitary accessories: soap dishes, toilet seats Complies with: U.S. FDA 21 CFR 181.32 European Food-Contact Compliance&& |
| Product Description | |
|---|---|
| Supplier | Trinseo |
| Generic | SAN |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Excellent Processability,Good Dimensional Stability,Food contact compliance,High Heat Resistance,Solvent resistance,HB |
| Availabilitys | Europe |
| Process Methods | Thermo forming |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.08 | g/cm³ | ASTM D792 |
| Density | 1.08 | g/cm³ | ISO 1183/B |
| Density | 1.08 | g/cm³ | ISO 1183-2 |
| Apparent density | 0.69 | g/cm³ | ASTM D1895 |
| Apparent density | 0.69 | g/cm³ | ISO 60 |
| Melt Flow Rate | ASTM D1238 | ||
| 220℃，10.0kg | 12 | g/10min | ASTM D1238 |
| 230℃，3.80kg | 4.0 | g/10min | ASTM D1238 |
| Melt Flow Rate | ISO 1133 | ||
| 220℃，10.0kg | 12 | g/10min | ISO 1133 |
| 230℃，3.80kg | 4.0 | g/10min | ISO 1133 |
| Melt Volume Rate | |||
| 220℃，10 kg | 12.0 | cm³/10min | ISO 1133 |
| Water absorption rate | |||
| saturated | 0.10 | % | ISO 62-2 |
| balance | 0.50 | % | ISO 62-2 |
| Viscosity value | 121 | cm³/g | ISO 307, 1157, 1628 2 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Unnotch Impact strength | |||
| 23℃ | 17 | kJ/m² | ISO 179 |
| Charpy impact strength | |||
| 23℃ | 17.0 | kJ/m² | ISO 179/1eU 2 |
| -30℃ | 18.0 | kJ/m² | ISO 179/1eU 2 |
| Notched impact strength of cantilever beam | |||
| 23℃ | 14 | kJ/m² | ISO 180 |
| Tensile Notch Impact Strength | |||
| 23℃ | 19.0 | kJ/m² | ISO 8256/1 2 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, annealed | 101 | ℃ | ASTM D648 |
| 1.8 MPa, annealed | 101 | ℃ | ISO 75-2/A |
| 1.8 MPa | 101 | ℃ | ISO 75-2 2 |
| Vicat Softening Temp | |||
| B50 | 104 | ℃ | ISO 306 2 |
| — | 101 | ℃ | ASTM D1525 4 |
| — | 110 | ℃ | ASTM D1525 5 |
| Linear coefficient of thermal expansion | |||
| TD | 6.0E-5 | 1/℃ | ISO 11359-2 2 |
| MD | 5.0E-5 | 1/℃ | DIN 53752 |
| MD | 5.0E-5 | 1/℃ | ISO 11359-2 2 |
| specific heat | 1380 | J/kg/℃ | ASTM D2766 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | > 1.0E+15 | ohms | IEC 60093 2 |
| Volume resistivity | > 1.0E+15 | ohms·cm | IEC 60093 2 |
| Dielectric strength | 9.1 | kV/mm | IEC 60243-1 |
| Relative permittivity | |||
| 100 Hz | 3.00 | IEC 60250 2 | |
| 1 MHz | 3.00 | IEC 60250 2 | |
| 1 MHz | 3.00 | IEC 60250 | |
| Dissipation factor | |||
| 1 MHz | 1.0E-4 | IEC 60250 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 1.60 mm | HB | UL 94 | |
| Flame retardant level | |||
| 1.60 mm | HB | ISO 1210 2 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 3700 | MPa | ASTM D638 |
| Tensile modulus | 3700 | MPa | ISO 527-2 |
| Tensile modulus | 3700 | MPa | ISO 527-2 2 |
| tensile strength | |||
| fracture | 70.0 | MPa | ISO 527-2/5 |
| fracture | 70.0 | MPa | ASTM D638 |
| yield | 72.0 | MPa | ISO 527-2 2 |
| Tensile strain | |||
| yield | 2.6 | % | ISO 527-2 2 |
| Nominal strain at break | 2.6 | % | ISO 527-2 2 |
| bending strength | 97.0 | MPa | ASTM D790 |
| bending strength | 97.0 | MPa | ISO 178 |
| Rockwell hardness | |||
| M-level | 83 | ASTM D785 | |
| M-level | 83 | ISO 2039-2 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 3. 0.20 in/min |
| 4. Rate A (50°C/h), Loading 2 (50 N) |
| 5. Rate B (120°C/h), Loading 1 (10 N) |
| 6. This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |