U-polymer PT-3020

About
P series resins are resins succeeding the characteristics of the neat polymer, U-100, and improved in flowability and optical properties. Among many super engineering plastics, the resins are few transparent polymer alloys that have heat resistance. The heat-stable P-series resins have variations different in heat resistance in the range from 150 to 175°C. There are few transparent heat-resistant resins among super engineering plastics, and thus P series resins are valuable. The resins have favorable weather resistance, and in particular, the P- 1001 resin is approved by SAE Standard (J576 and J578) and FMVSS Standard (108). Making the most of these characteristics, the resins may be used, for example, as the lenses for automobile lamps. High flow-type resins, P-1001A, and P-3001S, are also available for thin molding products.&&

About

P series resins are resins succeeding the characteristics of the neat polymer, U-100, and improved in flowability and optical properties. Among many super engineering plastics, the resins are few transparent polymer alloys that have heat resistance. The heat-stable P-series resins have variations different in heat resistance in the range from 150 to 175°C. There are few transparent heat-resistant resins among super engineering plastics, and thus P series resins are valuable. The resins have favorable weather resistance, and in particular, the P- 1001 resin is approved by SAE Standard (J576 and J578) and FMVSS Standard (108). Making the most of these characteristics, the resins may be used, for example, as the lenses for automobile lamps. High flow-type resins, P-1001A, and P-3001S, are also available for thin molding products.&&

Product Description
Supplier	UNITIKA
Generic	多芳基化合物
Material Status	Commercial: Active
Features	Good Rigidity,Weather resistance is good,Good flexibility,High impact resistance,Good Dimensional Stability,High elastic,Good liquidity,Optical performance,High Heat Resistance,Heat Stabilized,Amorphous
Availabilitys	North America,Asia Pacific

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.36	g/cm³	ASTM D792
Shrinkage rate
MD：3.0 mm	0.30-0.40	%	ASTM D995
TD：3.0 mm	0.40-0.50	%	ASTM D995
Water absorption rate
23℃，24hr	0.12	%	ASTM D570

MECHANICAL	Nominal value	Unit	Test method
tensile strength
23℃	67.0	MPa	ASTM D638
Tensile strain
Fracture, 23 ℃	6.0	%	ASTM D638
bending strength
23℃	111	MPa	ASTM D790
Bending modulus
23℃	3800	MPa	ASTM D790

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
1.8 MPa, unannealed	165	℃	ASTM D648
Linear coefficient of thermal expansion
MD	3.5E-5	1/℃	ASTM D696
TD	4.0E-5	1/℃	ASTM D696

FLAME CHARACTERISTICS	Nominal value	Test method
Flame retardant level
0.75mm	V-2	UL 94
3.00mm	V-2	UL 94

Process Conditions
injection	Nominal value	Unit	Test method
Drying temperature	140	°C
Drying time	6.0-24	Hr
Injection temperature
Rear barrel temperature	290-310	°C
Central temperature of the barrel	320-340	°C
Barrel front temperature	330-350	°C
Die temperature	330-350	°C
Mold temperature	110-130	°C

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.