| About |
|---|
| UBESTA 3035 JU5 is a high molecular weight Polyamide 12. It is plasticized and heat stabilized. Most suitable for super flexible hydraulic and pneumatic tubes.&& |
| Product Description | |
|---|---|
| Supplier | UBE |
| Generic | PA12 |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Good flexibility,Plasticizing,Heat Stabilized |
| Availabilitys | Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.03 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 235℃，2.16kg | 14 | g/10min | ISO 1133 |
| Shrinkage rate | ISO 294-4 | ||
| TD | 1.2 | % | ISO 294-4 |
| MD | 0.80 | % | ISO 294-4 |
| Water absorption rate | |||
| 23℃，24hr | 0.70 | % | ISO 62 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -40 ℃, completely fractured | 2.0 | kJ/m² | ISO 179/1eA |
| 23℃ | 无断裂 | ISO 179/1eA |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 70.0 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed | 40.0 | ℃ | ISO 75-2/A |
| Melting temperature | |||
| DSC | 162 | ℃ | ISO 3146 |
| Linear coefficient of thermal expansion | |||
| MD | 2.0E-4 | 1/℃ | ISO 11359-2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+10 | ohms·cm | IEC 60093 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 59 | ISO 868 | |
| Rockwell hardness | |||
| R-level | 28 | ISO 2039-2 | |
| tensile strength | |||
| yield | 30.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 300 | % | ISO 527-2 |
| Bending modulus | 200 | MPa | ISO 178 |
| bending strength | 10.0 | MPa | ISO 178 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |