| Udel® GF-110, resin is a 10% glass fiber reinforced polysulfone (PSU). Glass fiber substantially increases the rigidity, tensile strength, creep resistance, dimensional stability and chemical resistance of the polysulfone resin. The high performance properties and attractive price make these resins particularly effective alternatives to metals in many engineering applications. Natural: Udel® GF-110 NT&& |
| Product Description | |
|---|---|
| Supplier | Solvay |
| Generic | PSU |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good flexibility,Alkali resistant,Good Dimensional Stability,Hydrolysis stability,Ethanol tolerance,Acidproof,High Heat Resistance,Solvent resistance,Hydrocarbons,HB |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.33 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 343℃，2.16kg | 6.5 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD | 0.40 | % | ASTM D955 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 3720 | MPa | ASTM D638 |
| tensile strength | 77.9 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 4.0 | % | ASTM D638 |
| Bending modulus | 3790 | MPa | ASTM D790 |
| bending strength | 128 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 48 | J/m | ASTM D256 |
| Tensile impact strength | 101 | kJ/m² | ASTM D1822 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 179 | ℃ | ASTM D648 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 3.0E+16 | ohms·cm | ASTM D257 |
| Dielectric strength | 19 | kV/mm | ASTM D149 |
| Dielectric constant | ASTM D150 | ||
| 60 Hz | 3.18 | ASTM D150 | |
| 1 MHz | 3.15 | ASTM D150 | |
| Dissipation factor | ASTM D150 | ||
| 60 Hz | 7.0E-4 | ASTM D150 | |
| 1 MHz | 6.0E-3 | ASTM D150 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 3.20 mm | HB | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 149 to 163 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Processing (melt) temperature | 343 to 399 | °C | |
| Mold temperature | 121 to 163 | °C | |
| Injection speed | Fast | ||
| Back pressure | 0.345 to 0.689 | MPa | |
| Screw compression ratio | 2.0:1.0 | ||
| Notes |
|---|
| 1. Tested at 82 °C (180 °F) (Commercial Hot) |
| 2. Typical properties: these are not to be construed as specifications. |
| 3. These flammability ratings are not intended to reflect hazards presented by these or any other materials under actual fire conditions. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |