| About |
|---|
| Udel® P-1710 polysulfone (PSU) is a tough, rigid, high-strength thermoplastic that is suitable for continuous use up to 300°F (149°C). The resin is resistant to oxidation and hydrolysis and withstands prolonged exposure to high temperatures and repeated sterilization. Udel® P-1710 polysulfone is highly resistant to mineral acids, alkali and salt solutions. Its resistance to detergents and hydrocarbon oils is good, but it will be attacked by polar solvents such as ketones, chlorinated hydrocarbons and aromatic hydrocarbons. The resin is also highly resistant to degradation by gamma or electron beam radiation. Electrical properties are stable over a wide temperature range and after immersion in water or exposure to high humidity. Natural: Udel® P-1710 NT 15&& |
| Product Description | |
|---|---|
| Supplier | Solvay |
| Generic | PSU |
| Material Status | Commercial: Active |
| Features | Good flexibility,Alkali resistant,Good Dimensional Stability,Hydrolysis stability,Ethanol tolerance,Acidproof,High Heat Resistance,Solvent resistance,Hydrocarbons |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Process Methods | Film extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.24 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 343℃，2.16kg | 7.0 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD | 0.70 | % | ASTM D955 |
| Water absorption rate | |||
| 24hr | 0.30 | % | ASTM D570 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 2480 | MPa | ASTM D638 |
| tensile strength | 70.3 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 50 to 100 | % | ASTM D638 |
| Bending modulus | 2690 | MPa | ASTM D790 |
| bending strength | 106 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 69 | J/m | ASTM D256 |
| Tensile impact strength | 420 | kJ/m² | ASTM D1822 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 174 | ℃ | ASTM D648 |
| Linear coefficient of thermal expansion | |||
| MD | 5.6E-5 | 1/℃ | ASTM D696 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 5.0E+16 | ohms·cm | ASTM D257 |
| Dielectric strength | 17 | kV/mm | ASTM D149 |
| Dielectric constant | ASTM D150 | ||
| 60 Hz | 3.15 | ASTM D150 | |
| 1 kHz | 3.14 | ASTM D150 | |
| 1 MHz | 3.10 | ASTM D150 | |
| Dissipation factor | ASTM D150 | ||
| 60 Hz | 1.1E-3 | ASTM D150 | |
| 1 kHz | 1.3E-3 | ASTM D150 | |
| 1 MHz | 5.0E-3 | ASTM D150 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 135 to 163 | °C | |
| Drying time | 3.5 | hr | |
| Recommended injection volume | 50 to 75 | % | |
| Processing (melt) temperature | 329 to 385 | °C | |
| Mold temperature | 121 to 163 | °C | |
| Notes |
|---|
| 1. Tested at 82 °C (180 °F) (Commercial Hot) |
| 2. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |