| About |
|---|
| Udel® P-3703 is a high-flow grade of polysulfone intended for injection molding applications with thin walls or long flow lengths. This grade has higher flow than Udel® P-1700 and a slightly greater tendency to stress crack in some aggressive environments. Udel® polysulfone is a tough, rigid, high-strength thermoplastic that maintains its properties at temperatures from -101°C to 149°C (-150°F to 300°F). The heat deflection temperature at 1.8 MPa (264 psi) is 174°C (345°F). For most purposes, this resin is suitable for continuous use up to 149°C (300°F). The material is resistant to oxidation and hydrolysis and withstands prolonged exposure to high temperatures and repeated sterilization. Udel polysulfone is highly resistant to mineral acids, alkali and salt solutions. The resistance to detergents and hydrocarbon oils is good, but it will be attacked by polar solvents such as ketones, chlorinated hydrocarbons and aromatic hydrocarbons. Electrical properties of Udel polysulfone are stable over a wide temperature range and after immersion in water or exposure to high humidity. Natural: Udel® P-3703 NT 11&& |
| Product Description | |
|---|---|
| Supplier | Solvay |
| Generic | PSU |
| Material Status | Commercial: Active |
| Features | Good flexibility,Alkali resistant,High liquidity,Hydrolysis stability,Ethanol tolerance,Food contact compliance,Acidproof,High Heat Resistance,Solvent resistance,Hydrocarbons |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.24 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 343℃，2.16kg | 17 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD | 0.70 | % | ASTM D955 |
| Water absorption rate | |||
| 24hr | 0.30 | % | ASTM D570 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 2480 | MPa | ASTM D638 |
| tensile strength | |||
| fracture | 70.3 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 50 to 100 | % | ASTM D638 |
| Bending modulus | 2690 | MPa | ASTM D790 |
| bending strength | 106 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 69 | J/m | ASTM D256 |
| Tensile impact strength | 420 | kJ/m² | ASTM D1822 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 174 | ℃ | ASTM D648 |
| Linear coefficient of thermal expansion | |||
| MD | 5.6E-5 | 1/℃ | ASTM D696 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 5.0E+16 | ohms·cm | ASTM D257 |
| Dielectric strength | 17 | kV/mm | ASTM D149 |
| Dielectric constant | ASTM D150 | ||
| 60 Hz | 3.03 | ASTM D150 | |
| 1 kHz | 3.04 | ASTM D150 | |
| 1 MHz | 3.02 | ASTM D150 | |
| Dissipation factor | ASTM D150 | ||
| 60 Hz | 1.1E-3 | ASTM D150 | |
| 1 kHz | 1.3E-3 | ASTM D150 | |
| 1 MHz | 5.0E-3 | ASTM D150 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 135 to 163 | °C | |
| Drying time | 3.5 | hr | |
| Recommended injection volume | 50 to 75 | % | |
| Processing (melt) temperature | 329 to 385 | °C | |
| Mold temperature | 121 to 163 | °C | |
| Notes |
|---|
| 1. Maximum Temperature of Use: 149°C (300°F) |
| 2. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |