| Standard flow Polyetherimide (Tg 217C). ECO Conforming. US FDA and EU Food Contact compliant. UL94 V0, V2 and 5VA listing. Effective June 2007, this grade will no longer be supported with biocompatibility information and should not be used for medical applications which require biocompatibility. Alternative grade HU1100.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | Polyetherimide |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good surface appearance,High liquidity,Heat Stabilized,V-2,V-0,5VA |
| Availabilitys | Africa & Middle East ,North America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.36 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 337℃，6.60kg | 8.8 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.50 to 0.70 | % | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 3720 | MPa | ASTM D638 |
| tensile strength | |||
| yield | 110 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 70 | % | ASTM D638 |
| Bending modulus | |||
| 100 mm span | 3720 | MPa | ASTM D790 |
| bending strength | |||
| Yield, 100 mm span | 165 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 37 | J/m | ASTM D256 |
| Impact strength of cantilever beam notch | |||
| 3.2mm | 1500 | J/m | ASTM D256 |
| Drop hammer impact | |||
| 23℃ | 21.7 | J | ASTM D3029 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 6.4 mm | 199 | ℃ | ASTM D648 |
| Relative temperature index | |||
| Electrical performance | 170 | ℃ | UL 746 |
| Strength mechanical performance | 170 | ℃ | UL 746 |
| Impact mechanical performance | 170 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Arc resistance | PLC 5 | ASTM D495 | |
| Compared to the leakage tracing index | PLC 4 | UL 746 | |
| High Arc Burning Index (HAI) | PLC 3 | UL 746 | |
| High voltage arc marking rate | |||
| HVTR | PLC 2 | UL 746 | |
| Hot wire ignition | |||
| HWI | PLC 1 | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 0.40 mm | V-2 | UL 94 | |
| 0.75 mm | V-0 | UL 94 | |
| 3.00 mm | 5VA | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 149 | °C | |
| Drying time | 4.0 to 6.0 | hr | |
| Drying time, maximum | 24 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Recommended injection volume | 40 to 60 | % | |
| Barrel rear temperature | 332 to 399 | °C | |
| Barrel middle temperature | 338 to 399 | °C | |
| Barrel front temperature | 343 to 399 | °C | |
| Nozzle temperature | 343 to 399 | °C | |
| Processing (melt) temperature | 349 to 399 | °C | |
| Mold temperature | 135 to 163 | °C | |
| Back pressure | 0.345 to 0.689 | MPa | |
| Screw speed | 40 to 70 | rpm | |
| Vent depth | 0.025 to 0.076 | mm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.20 in/min |
| 3. Type I, 0.20 in/min |
| 4. 0.10 in/min |
| 5. Tungsten Electrode |
| 6. Surface |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |