| ULTEM™ 1285 resin Transparent Polyetherimide blend. ECO Conforming. US FDA and EU Food Contact Compliant in recognized colors.&&ULTEM™ 1285 resin Transparent Polyetherimide blend. ECO Conforming. US FDA and EU Food Contact compliant in recognized colors.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | Polyetherimide |
| Material Status | Commercial: Active |
| Features | Food contact compliance,ECO |
| Availabilitys | North America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.29 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 295℃，6.60kg | 8.1 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.60 to 0.70 | % | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 3380 | MPa | ASTM D638 |
| tensile strength | |||
| fracture | 82.7 | MPa | ASTM D638 |
| yield | 110 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 60 | % | ASTM D638 |
| Bending modulus | |||
| 100 mm span | 3380 | MPa | ASTM D790 |
| bending strength | |||
| Yield, 100 mm span | 165 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 27 | J/m | ASTM D256 |
| Impact strength of cantilever beam notch | |||
| 3.2mm | 950 | J/m | ASTM D256 |
| Dart impact equipped with measuring instruments | |||
| 23℃，Total Energy | 40.7 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 6.4 mm | 165 | ℃ | ASTM D648 |
| Vicat Softening Temp | 181 | ℃ | ASTM D1525 5 |
| Linear coefficient of thermal expansion | |||
| TD：-40~40℃ | 4.9E-5 | 1/℃ | ASTM E831 |
| MD：-40~40℃ | 4.9E-5 | 1/℃ | ASTM E831 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 121 to 149 | °C | |
| Drying time | 4.0 to 8.0 | hr | |
| Drying time, maximum | 24 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Recommended injection volume | 40 to 60 | % | |
| Barrel rear temperature | 282 to 316 | °C | |
| Barrel middle temperature | 288 to 321 | °C | |
| Barrel front temperature | 293 to 327 | °C | |
| Nozzle temperature | 299 to 332 | °C | |
| Processing (melt) temperature | 299 to 332 | °C | |
| Mold temperature | 93 to 149 | °C | |
| Back pressure | 0.689 to 1.38 | MPa | |
| Screw speed | 50 to 100 | rpm | |
| Vent depth | 0.025 to 0.076 | mm | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |