| About |
|---|
| 20% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C). ECO Conforming. US FDA Food Contact compliant in recognized colors.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | Polyetherimide |
| Material Status | Commercial: Active |
| Features | Good liquidity,Food contact compliance,ECO |
| Availabilitys | North America,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.42 | g/cm³ | ISO 1183 |
| Water absorption rate | |||
| Saturation, 23 ℃ | 1.0 | % | ISO 62 |
| Equilibrium, 23 ℃, 50% RH | 0.55 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 6900 | MPa | ASTM D638 |
| Tensile modulus | 6800 | MPa | ISO 527-1-2 |
| tensile strength | |||
| fracture | 140 | MPa | ASTM D638 |
| fracture | 140 | MPa | ISO 527-2/5 |
| yield | 139 | MPa | ASTM D638 |
| yield | 140 | MPa | ISO 527-2/5 |
| Tensile strain | |||
| fracture | 5.0 | % | ISO 527-2/5 |
| yield | 5.0 | % | ISO 527-2/5 |
| yield | 4.0 | % | ASTM D638 |
| Bending modulus | 6500 | MPa | ISO 178 |
| 50 mm span | 6890 | MPa | ASTM D790 |
| bending strength | 210 | MPa | ISO 178 |
| bending strength | |||
| Yield, 50 mm span | 227 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 8.0 | kJ/m² | ISO 179/1eA |
| Impact strength of cantilever beam notch | ISO 180/1A | ||
| 23℃ | 480 | J/m | ASTM D4812 |
| -30℃ | 5.0 | kJ/m² | ISO 180-1A |
| 23℃ | 5.0 | kJ/m² | ISO 180-1A |
| Dart impact equipped with measuring instruments | |||
| 23℃，Total Energy | 13.0 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 6.4 mm | 211 | ℃ | ASTM D648 |
| Vicat Softening Temp | 226 | ℃ | ASTM D1525 9 |
| Vicat Softening Temp | |||
| B50 | 212 | ℃ | ISO 306 |
| B120 | 218 | ℃ | ISO 306/B120 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 150 | °C | |
| Drying time | 4.0 to 6.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Hopper temperature | 80 to 120 | °C | |
| Barrel rear temperature | 350 to 400 | °C | |
| Barrel middle temperature | 360 to 410 | °C | |
| Barrel front temperature | 370 to 420 | °C | |
| Nozzle temperature | 360 to 410 | °C | |
| Processing (melt) temperature | 370 to 410 | °C | |
| Mold temperature | 140 to 180 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Tensile Bar |
| 3. 0.079 in/min |
| 4. at Break |
| 5. 80*10*4 sp=62mm |
| 6. 80*10*4 mm |
| 7. 120*10*4 mm |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |