| About |
|---|
| Glass fiber, PTFE, and Graphite filled, standard flow Polyetherimide (Tg 217C). ECO Conforming, UL94 V0 listing.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | Polyetherimide |
| Material Status | Commercial: Active |
| Features | Low coefficient of friction,Flame Characteristics,Good wear resistance,ECO,Amorphous,V-0 |
| Availabilitys | North America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.67 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 337℃，6.60kg | 3.1 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.20 to 0.30 | % | Internal Method |
| Water absorption rate | |||
| 24hr | 0.11 | % | ASTM D570 |
| K (wear) coefficient | Internal Method | ||
| — | 62.0 | Internal Method | |
| — | 1900 | Internal Method | |
| PV Limit | 2.1 | MPa·m/s | Internal Method |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 64 | J/m | ASTM D256 |
| 23℃ | 160 | J/m | ASTM D4812 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 6.4 mm | 212 | ℃ | ASTM D648 |
| Vicat Softening Temp | 234 | ℃ | ASTM D1525 7 |
| Linear coefficient of thermal expansion | |||
| MD | ASTM E831 | ||
| -40 to 40 ℃ | 1.6E-5 | cm/cm/℃ | ASTM E831 |
| -20 to 150 ℃ | 1.6E-5 | cm/cm/℃ | ASTM E831 |
| Relative temperature index | |||
| Electrical performance | 105 | ℃ | UL 746 |
| Strength mechanical performance | 105 | ℃ | UL 746 |
| Impact mechanical performance | 105 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Compared to the leakage tracing index | PLC 4 | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 0.80 mm | V-0 | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| fracture | 82.7 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 1.2 | % | ASTM D638 |
| Bending modulus | |||
| 100 mm span | 8830 | MPa | ASTM D790 |
| bending strength | |||
| Fracture, 100 mm span | 138 | MPa | ASTM D790 |
| Yield, 100 mm span | 114 | MPa | ASTM D790 |
| friction coefficient | ASTM D1894 | ||
| Steel – Dynamic | 0.24 | ASTM D1894 | |
| Steel – Static | 0.25 | ASTM D1894 | |
| Taber abraser | |||
| 1000 cycles, 1000 g, CS-17 wheels | 33.0 | mg | ASTM D1044 |
| Rockwell hardness | |||
| M-level | 85 | ASTM D785 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 135 | °C | |
| Drying time | 4.0 to 6.0 | hr | |
| Drying time, maximum | 10 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Recommended injection volume | 40 to 60 | % | |
| Barrel rear temperature | 338 to 360 | °C | |
| Barrel middle temperature | 343 to 366 | °C | |
| Barrel front temperature | 349 to 371 | °C | |
| Nozzle temperature | 349 to 371 | °C | |
| Processing (melt) temperature | 349 to 371 | °C | |
| Mold temperature | 135 to 163 | °C | |
| Back pressure | 0.345 to 0.689 | MPa | |
| Screw speed | 40 to 70 | rpm | |
| Vent depth | 0.025 to 0.076 | mm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. PV=2000 psi-fpm |
| 3. 0.51 m/s |
| 4. Type I, 0.20 in/min |
| 5. 0.10 in/min |
| 6. Rate A (50°C/h), Loading 2 (50 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |