| About |
|---|
| High flow Polyetherimide blend. Meets FAR 25.853 and OSU 65/65 with low toxicity, smoke, and flame evolution. ECO Conforming.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | Polyetherimide |
| Material Status | Commercial: Active |
| Features | Low smoke,High liquidity,Low toxicity,ECO |
| Availabilitys | North America,Asia Pacific,Europe |
| Process Methods | Profile extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.30 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 295℃，6.60kg | 2.4 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| TD：3.2 mm | 0.50 to 0.70 | % | Internal Method |
| MD：3.2 mm | 0.50 to 0.70 | % | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 3310 | MPa | ASTM D638 |
| tensile strength | |||
| yield | 96.5 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 85 | % | ASTM D638 |
| Bending modulus | |||
| 100 mm span | 3240 | MPa | ASTM D790 |
| bending strength | |||
| Fracture, 100 mm span | 141 | MPa | ASTM D790 |
| Yield, 100 mm span | 145 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 69 | J/m | ASTM D256 |
| Impact strength of cantilever beam notch | |||
| 3.2mm | 2100 | J/m | ASTM D256 |
| Drop hammer impact | |||
| 23℃ | 35.3 | J | ASTM D3029 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 6.4 mm | 189 | ℃ | ASTM D648 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| FAA Flammability | SECT A-1 | FAR 25.853 | |
| Halogen Content | 0 | Internal Method | |
| OSU total heat release | 10.0 | kW·min/m² | FAR 25.853 |
| Vertical combustion test | FAR 25.853 | ||
| Test a（60 s），passes at | 1.0 | sec | FAR 25.853 |
| Test b（12 s），passes at | 0.0 | sec | FAR 25.853 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Extrusion | Nominal value | Unit | Test method |
| Drying temperature | 135 | °C | |
| Drying time | 4.0 to 6.0 | hr | |
| Drying time, maximum | 10 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Recommended injection volume | 40 to 60 | % | |
| Barrel rear temperature | 338 to 360 | °C | |
| Barrel middle temperature | 343 to 366 | °C | |
| Barrel front temperature | 349 to 371 | °C | |
| Nozzle temperature | 349 to 371 | °C | |
| Processing (melt) temperature | 349 to 371 | °C | |
| Mold temperature | 135 to 163 | °C | |
| Back pressure | 0.345 to 0.689 | MPa | |
| Screw speed | 40 to 70 | rpm | |
| Vent depth | 0.025 to 0.076 | mm | |
| Drying temperature | 130 to 140 | °C | |
| Drying time | 4.0 to 6.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Hopper temperature | 80 to 100 | °C | |
| Barrel 1 zone temperature | 280 to 300 | °C | |
| Barrel 2 zone temperature | 295 to 320 | °C | |
| Barrel 3 zone temperature | 305 to 330 | °C | |
| Barrel 4 zone temperature | 310 to 335 | °C | |
| Connector temperature | 285 to 335 | °C | |
| Melt temperature | 295 to 330 | °C | |
| Nozzle temperature | 275 to 330 | °C | |
| Calibration temperature, first time | 140 to 170 | °C | |
| Calibration Temp, Second | 90 to 130 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.20 in/min |
| 3. Type I, 0.20 in/min |
| 4. 0.10 in/min |
| 5. FAR 25.853 A/B |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |