| About |
|---|
| High flow Polyetherimide blend for automotive lighting applications where highly metallized, reflective surfaces are required. Haze onset temperature of 195C (SABIC test method).&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PEI+PCE |
| Material Status | Commercial: Active |
| Features | High liquidity |
| Availabilitys | North America,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.26 | g/cm³ | ASTM D792 |
| Density | 1.27 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 337℃，6.60kg | 24 | g/10min | ASTM D1238 |
| Melt Volume Rate | |||
| 340℃，5 kg | 16.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| TD | 0.50 to 0.70 | % | Internal Method |
| MD：3.2 mm | 0.50 to 0.70 | % | Internal Method |
| Water absorption rate | |||
| Saturation, 23 ℃ | 0.90 | % | ISO 62 |
| Equilibrium, 23 ℃, 50% RH | 0.50 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 3000 | MPa | ISO 527-1-2 |
| tensile strength | |||
| yield | 96.5 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 70 | % | ASTM D638 |
| Bending modulus | 3100 | MPa | ISO 178 |
| 100 mm span | 3170 | MPa | ASTM D790 |
| bending strength | |||
| Yield, 100 mm span | 145 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30℃ | 4.0 | kJ/m² | ISO 179/1eA |
| 23℃ | 4.0 | kJ/m² | ISO 179/1eA |
| Impact strength of cantilever beam notch | ISO 180/1A | ||
| 23℃ | 53 | J/m | ASTM D256 |
| 23℃ | 2100 | J/m | ASTM D4812 |
| -30℃ | 5.0 | kJ/m² | ISO 180-1A |
| 23℃ | 5.0 | kJ/m² | ISO 180-1A |
| Impact strength of cantilever beam notch | |||
| 3.2mm | 2100 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 6.4 mm | 190 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 100 mm span | 180 | ℃ | ISO 75-2/Ae |
| 0.45 MPa, unannealed, 100 mm span | 195 | ℃ | ISO 75-2/Be |
| Vicat Softening Temp | |||
| B120 | 205 | ℃ | ISO 306/B120 |
| Linear coefficient of thermal expansion | |||
| TD：23~150℃ | 6.0E-5 | 1/℃ | ISO 11359-2 |
| MD：23~150℃ | 6.0E-5 | 1/℃ | ISO 11359-2 |
| Thermal conductivity coefficient | 0.23 | W/m/K | ISO 8302 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Metallized Haze Onset | 195 | ℃ | Internal Method |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 130 to 140 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Hopper temperature | 80 to 100 | °C | |
| Barrel rear temperature | 320 to 340 | °C | |
| Barrel middle temperature | 330 to 350 | °C | |
| Barrel front temperature | 340 to 360 | °C | |
| Nozzle temperature | 340 to 360 | °C | |
| Processing (melt) temperature | 340 to 380 | °C | |
| Mold temperature | 125 to 140 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Tensile Bar |
| 3. Type I, 0.20 in/min |
| 4. 0.10 in/min |
| 5. 0.079 in/min |
| 6. 80*10*4 sp=62mm |
| 7. 80*10*4 mm |
| 8. 120*10*4 mm |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |