| Improved ductility, transparent, standard flow Polyetherimide blend (Tg 200C) with internal mold release and enhanced ductility. ECO Conforming.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | Polyetherimide |
| Material Status | Commercial: Active |
| Features | Ductility,ECO |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.28 | g/cm³ | ASTM D792 |
| Density | 1.28 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 337℃，6.60kg | 23 | g/10min | ASTM D1238 |
| Melt Volume Rate | |||
| 360℃，5 kg | 28.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.50 to 0.70 | % | Internal Method |
| Water absorption rate | |||
| Saturation, 23 ℃ | 0.37 | % | ISO 62 |
| Equilibrium, 23 ℃, 50% RH | 0.090 | % | ISO 62 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 2.0 | kJ/m² | ISO 179/1eA |
| Impact strength of cantilever beam notch | ASTM D256 | ||
| -30℃ | 38 | J/m | ASTM D256 |
| 23℃ | 35 | J/m | ASTM D256 |
| Impact strength of cantilever beam notch | ISO 180/1A | ||
| -30℃ | 2.0 | kJ/m² | ISO 180-1A |
| 23℃ | 2.0 | kJ/m² | ISO 180-1A |
| Impact strength of cantilever beam notch | ASTM D4812 | ||
| -30℃ | No Break | ASTM D4812 | |
| 23℃ | No Break | ASTM D4812 | |
| Impact strength of cantilever beam notch | |||
| 3.2mm | 2100 | J/m | ASTM D256 |
| Dart impact equipped with measuring instruments | ASTM D3763 | ||
| -20℃，Total Energy | 10.0 | J | ASTM D3763 |
| 23℃，Total Energy | 50.0 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 1.8 MPa, unannealed, 100 mm span | 168 | ℃ | ISO 75-2/Ae |
| 1.8 MPa, unannealed, 3.2 mm | 173 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 6.4 mm | 178 | ℃ | ASTM D648 |
| Vicat Softening Temp | 192 | ℃ | ASTM D1525 10 |
| Vicat Softening Temp | |||
| B50 | 192 | ℃ | ISO 306 |
| B120 | 195 | ℃ | ISO 306/B120 |
| Linear coefficient of thermal expansion | |||
| TD：23~150℃ | 5.5E-5 | 1/℃ | ISO 11359-2 |
| TD：-20：150℃ | 6.0E-5 | 1/℃ | ASTM E831 |
| MD：23~150℃ | 5.5E-5 | 1/℃ | ISO 11359-2 |
| MD：-20~150℃ | 6.0E-5 | 1/℃ | ASTM E831 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.6E+17 | ohms | ASTM D257 |
| Volume resistivity | 1.0E+17 | ohms·cm | ASTM D257 |
| Dissipation factor | |||
| 1 MHz | 6.1E-3 | ASTM D150 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 3210 | MPa | ASTM D638 |
| Tensile modulus | 2500 | MPa | ISO 527-1-2 |
| tensile strength | |||
| fracture | 80.0 | MPa | ISO 527-2/5 |
| fracture | 85.0 | MPa | ASTM D638 |
| yield | 103 | MPa | ASTM D638 |
| yield | 98.0 | MPa | ISO 527-2/5 |
| Tensile strain | |||
| fracture | 80 | % | ISO 527-2/5 |
| fracture | 80 | % | ASTM D638 |
| yield | 7.0 | % | ASTM D638 |
| yield | 7.0 | % | ISO 527-2/5 |
| Bending modulus | 3100 | MPa | ISO 178 |
| 50 mm span | 3500 | MPa | ASTM D790 |
| bending strength | 135 | MPa | ISO 178 |
| bending strength | |||
| Yield, 50 mm span | 145 | MPa | ASTM D790 |
| Rockwell hardness | |||
| M-level | 108 | ASTM D785 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 135 | °C | |
| Drying time | 4.0 to 6.0 | hr | |
| Drying time, maximum | 12 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Recommended injection volume | 40 to 60 | % | |
| Barrel rear temperature | 310 to 332 | °C | |
| Barrel middle temperature | 321 to 343 | °C | |
| Barrel front temperature | 332 to 354 | °C | |
| Nozzle temperature | 327 to 349 | °C | |
| Processing (melt) temperature | 332 to 354 | °C | |
| Mold temperature | 93 to 135 | °C | |
| Back pressure | 0.345 to 0.689 | MPa | |
| Screw speed | 40 to 70 | rpm | |
| Vent depth | 0.025 to 0.076 | mm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.20 in/min |
| 3. Type I, 0.20 in/min |
| 4. 0.051 in/min |
| 5. 0.079 in/min |
| 6. at Yield |
| 7. 80*10*4 sp=62mm |
| 8. 80*10*4 mm |
| 9. 120*10*4 mm |
| 10. Rate A (50°C/h), Loading 2 (50 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |