| ULTEM™ AM1010F filament is a polyetherimide product for 3D printing applications manufactured from ULTEM™ 1010 resin. The filament provides high heat resistance and mechanical strength, is UL94 V-0 compliant at 1.5 mm and 5VA compliant at 3.0 mm. |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | Polyetherimide |
| Material Status | Commercial: Active |
| Availabilitys | North America,Latin America,Europe |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| Tensile modulus | |||
| XY direction | 2750 | MPa | |
| XZ direction | 2870 | MPa | |
| ZX direction | 2840 | MPa | |
| Tensile strength | |||
| XY direction: fracture | 73.0 | MPa | |
| XZ direction: fracture | 80.0 | MPa | |
| ZX direction: fracture | 34.0 | MPa | |
| Tensile strain | |||
| XY direction, fracture | 4.0 | % | |
| XZ direction, fracture | 3.8 | % | |
| ZX direction, fracture | 1.3 | % | |
| Bending modulus | |||
| XY direction | 2520 | MPa | |
| XZ direction | 2840 | MPa | |
| ZX direction | 2380 | MPa | |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| XY direction, 23 ℃ | 31 | J/m | |
| XZ direction, 23 ℃ | 37 | J/m | |
| ZX direction, 23 ℃ | 30 | J/m | |
| Notched impact strength of cantilever beam | |||
| ZX direction: 23 ℃ | 130 | J/m | |
| XZ direction: 23 ℃ | 240 | J/m | |
| XY direction: 23 ℃ | 270 | J/m |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| XY direction: 1.8 MPa, unannealed, 3.20 mm | 211 | ℃ | |
| XZ direction: 1.8 MPa, unannealed, 3.20 mm | 210 | ℃ | |
| ZX direction: 1.8 MPa, unannealed, 3.20 mm | 208 | ℃ | |
| Vicat Softening Temp | 220 | ℃ | ASTM D1525 4 |
| Linear coefficient of thermal expansion | |||
| Flow: XY direction | 5.1E-5 | 1/℃ | |
| Flow: XZ direction | 5.3E-5 | 1/℃ | |
| Flow: ZX direction | 5.3E-5 | 1/℃ | |
| TD: XZ direction | 5.2E-5 | 1/℃ | |
| TD: ZX direction | 5.3E-5 | 1/℃ | |
| TD: XY direction | 5.3E-5 | 1/℃ |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | |||
| XY direction | 6.2E+14 | ohms·cm | |
| XZ direction | 1.3E+15 | ohms·cm | |
| Dielectric constant | |||
| XZ direction: 1.90 GHz | 2.90 | ||
| XY direction: 1.90 GHz | 2.90 | ||
| Dissipation factor | |||
| XY direction: 1.90 GHz | 3.0E-3 | ||
| XZ direction: 1.90 GHz | 3.0E-3 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| XZ direction, 1.50 mm | V-0 | ||
| XY direction, 1.50 mm | V-0 | ||
| ZX direction, 1.50 mm | V-0 | ||
| XY direction, 3.00 mm | 5VA | ||
| FAA Flammability（1.50 mm） | Passed | FAR 25.853 | |
| OSU peak heat release rate -5 minute test (1.50 mm) | 23.0 | kW/m² | FAR 25.853 |
| OSU total heat release -2 minute test (1.50 mm) | 5.00 | kW·min/m² | FAR 25.853 |
| Vertical combustion test | |||
| 12s，passes at：1.50 mm | 0.0 | sec | |
| 60s，passes at：1.50 mm | 2.0 | sec |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |