| About |
|---|
| 40% Glass fiber filled, standard flow Polyetherimide (Tg 217?C). Specific grade-colors are designed and certified for use in Potable Water applications. KTW, WRAS, ACS, NSF-61 and W270 certified. US FDA and European Food Contact approved.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | Polyetherimide |
| Material Status | Commercial: Active |
| Features | Food contact compliance |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.61 | g/cm³ | ISO 1183 |
| Melt Volume Rate | |||
| 360℃，5 kg | 5.00 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| MD | 0.10 to 0.30 | % | Internal Method |
| Water absorption rate | ISO 62 | ||
| Saturation, 23 ℃ | 0.80 | % | |
| Equilibrium, 23 ℃, 50% RH | 0.40 | % | |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Unnotch Impact strength | ISO 179/1eU | ||
| -30℃ | 40 | kJ/m² | |
| 23℃ | 40 | kJ/m² | |
| Notched impact strength of cantilever beam | ISO 180/1U | ||
| -30℃ | 35 | kJ/m² | |
| 23℃ | 35 | kJ/m² |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, 100 mm span | 215 | ℃ | ISO 75-2/Be |
| 1.8 MPa, unannealed, 100 mm span | 210 | ℃ | ISO 75-2/Ae |
| Vicat Softening Temp | |||
| A50 | 230 | ℃ | ISO 306/A50 |
| B50 | 217 | ℃ | ISO 306 |
| B120 | 225 | ℃ | ISO 306/B120 |
| Ball pressure test | |||
| 125℃ | Pass | IEC 60695-10-2 | |
| Linear coefficient of thermal expansion | ISO 11359-2 | ||
| MD：23~150℃ | 1.5E-5 | 1/℃ | |
| TD：23~150℃ | 4.5E-5 | 1/℃ | |
| Thermal conductivity coefficient | 0.33 | W/m/K | ISO 8302 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Extreme oxygen index | 48 | % | ISO 4589-2 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Ball hardness | |||
| H358/30 | 170 | MPa | ISO 2039-1 |
| Tensile modulus | 11500 | MPa | ISO 527-1-2 |
| tensile strength | |||
| fracture | 180 | MPa | ISO 527-2/5 |
| Tensile strain | |||
| fracture | 2.0 | % | ISO 527-2/5 |
| Bending modulus | 10000 | MPa | ISO 178 |
| bending strength | 240 | MPa | ISO 178 |
| Taber abraser | |||
| 1000 cycles, 1000 g, CS-17 wheels | 20.0 | mg | Internal Method |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 150 | °C | |
| Drying time | 4.0 to 6.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Hopper temperature | 80.0 to 100 | °C | |
| Barrel rear temperature | 350 to 390 | °C | |
| Barrel middle temperature | 370 to 410 | °C | |
| Barrel front temperature | 380 to 420 | °C | |
| Nozzle temperature | 370 to 410 | °C | |
| Processing (melt) temperature | 370 to 410 | °C | |
| Mold temperature | 140 to 180 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Tensile Bar |
| 3. 0.079 in/min |
| 4. at Break |
| 5. 80*10*4 sp=62mm |
| 6. 80*10*4 mm |
| 7. 120*10*4 mm |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |