ULTEM™ RESIN MD131

About

Product Description
Supplier	SABIC
Generic	Polyetherimide
Material Status	Commercial: Active
Features	High liquidity

Technical Data
MECHANICAL	Nominal value	Unit	Test method
Tensile Strength
yld	110	MPa	ASTM D638
brk	105	MPa	ASTM D638
yld	105	MPa	ISO 527-2
brk	85	MPa	ISO 527-2
Tensile Strain
yld	7	%	ASTM D638
brk	60	%	ASTM D638
yld	6	%	ISO 527
brk	60	%	ISO 527
Tensile Modulus
	3590	MPa	ASTM D638
	3200	MPa	ISO 527
Flexural Strength
yld	167	MPa	ASTM D790
yld	165	MPa	ASTM D790
yld	160	MPa	ISO 178
Flexural Modulus
	3550	MPa	ASTM D790
	3520	MPa	ASTM D790
	3300	MPa	ISO 178
Rockwell Hardness	109		ASTM D-785
Taber Abrasion	10	mg/1000cy	ASTM D1044
ball-indentation hardness	140	MPa	ISO 2039-1

IMPACT	Nominal value	Unit	Test method
Izod Unnotched Impact strength
23℃	1335	J/m	ASTM D4812
23℃	NB	KJ/m²	ISO 180/1U
-30℃	NB	KJ/m²	ISO 180/1U
Izod Notched Impact strength
23℃	32	J/m	ASTM D256
-30℃	35	J/m	ASTM D256
	1174	J/m	ASTM D256
23℃	5	KJ/m²	ISO 180/1A
23℃	5	KJ/m²	ISO 180/1A
Charpy notched Impact strength	3	kJ/m²	ISO 179/1eA

THERMAL	Nominal value	Unit	Test method
Vicat Softening Temperature
Rate B/50	218	℃	ASTM D1525
Rate A/50	215	℃	ISO 306/B
Rate B/50	211	℃	ISO 306/B
Rate B/120	212	℃	ISO 306/B
HDT
0.45 MPa	205	℃	ASTM D648
1.82 MPa	197	℃	ASTM D648
0.45 MPa	207	℃	ASTM D648
1.82 MPa	198	℃	ASTM D648
0.45 MPa	200	℃	ISO 75-1/-2
1.8 MPa	190	℃	ISO 75-1/-2
1.8 MPa	190	℃	ISO 75-1/-2
Coeff.of linear therm expansion
-40°C to 150°C，flow	5.5	×10-5/℃	ASTM E831
-40°C to 150°C，xflow	5.5	×10-5/℃	ASTM E831
23°C to 150°C, flow	5	×10-5/℃	ISO 11359-2
23°C to 150°C, xflow	5	×10-5/℃	ISO 11359-2
Thermal Conductivity
	0.22	W/m/℃	ASTM C177
	0.21	W/m/℃	ISO 8302
Ball Pressure Test	passes		IEC 60695-10-2

PHYSICAL	Nominal value	Unit	Test method
Specific Gravity	1.27		ASTM D792
Water Absorption
24 hours	0.25	%	ASTM D570
equilibrium, 23C	0.25	%	ASTM D570
23°C/sat	1.25	%	ISO 62
Mold Shrinkage
on Tensile Bar, flow	0.5-0.7	%
flow, 3.2 mm	0.5-0.7	%
xflow, 3.2 mm	0.5-0.7	%
Melt Flow Rate
337°C/6.6 kgf	17.8	g/10min	ASTM D1238
Melt Volume Rate
340°C/5.0 kg	13	cm³/10min	ISO 1133
360°C/5.0 kg	25	cm³/10min	ISO 1133
Moisture Absorption
23°C / 50% RH	0.7	%	ISO 62
Density	1.27	g/cm³	ISO 1183

ELECTRICAL	Nominal value	Unit	Test method
Volume Resistivity
	1E17	ohm·cm	ASTM D257
	1E15	ohm·cm	IEC 60093
Dielectric Strength
in air, 1.6 mm	32.6	kV/mm	ASTM D149
in oil, 1.6 mm	27.9	kV/mm	ASTM D149
in oil, 0.8 mm	33	kV/mm	IEC 60243-1
in oil, 1.6 mm	25	kV/mm	IEC 60243-1
in oil, 3.2 mm	16	kV/mm	IEC 60243-1
Relative Permittivity
1 kHz	3.15		ASTM D150
1 MHz	2.9		IEC 60250
50/60 Hz	2.9		IEC 60250
Dissipation Factor
1 kHz	0.0013		ASTM D150
2450 MHz	0.0025		ASTM D150
50/60 Hz	0.0005		IEC 60250
1 MHz	0.006		IEC 60250
2450 MHz	0.0025		IEC 60250
Comparative Tracking Index
	150	V	IEC 60112
	100	V	IEC 60112
Surface Resistivity	>1E15	ohm	IEC 60093

FLAME CHARACTERISTICS	Nominal value	Unit	Test method
Oxygen Index
	44	%	ASTM D2863
	47	%	ISO 4589-2
Glow Wire Flammability Index(GWFI)
3.2 mm	960	℃	IEC 60695-2-12


Nominal value	Unit	Test method
150	℃
4-6	hr
24	hr
0.02	%
350-400	℃
345-400	℃
345-400	℃
340-400	℃
340-400	℃
130-165	℃
0.3-0.7	MPa
40-70	rpm
40-60	%
0.025-0.076	mm

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.