| About |
|---|
| Ultradur B 4300 G6 HR LS BK15045 is a hydrolysis resistant, laser markable, pigmented black, 30% fiberglass reinforced PBT for rigid and dimensionally stable technical parts.&& |
| Product Description | |
|---|---|
| Supplier | BASF |
| Generic | polybutylene terephthalate |
| Material Status | Commercial: Active |
| Features | Hydrolysis stability,Laser engraving |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.52 | g/cm³ | ISO 1183 |
| Viscosity value | |||
| Reduced viscosity | 105.0 | ml/g | ISO 1628 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 23℃ | 8500 | MPa | ISO 527-2 |
| tensile strength | |||
| Fracture, 23 ℃ | 130 | MPa | ISO 527-2 |
| Tensile strain | |||
| Fracture, 23 ℃ | 3.5 | % | ISO 527-2 |
| Bending modulus | |||
| 23℃ | 8100 | MPa | ISO 178 |
| bending strength | |||
| 23℃ | 188 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 11 | kJ/m² | ISO 179 |
| Charpy Unnotch Impact strength | ISO 179 | ||
| -30℃ | 62 | kJ/m² | ISO 179 |
| 23℃ | 69 | kJ/m² | ISO 179 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 205 | ℃ | ISO 75-2/A |
| 0.45 MPa, unannealed | 220 | ℃ | ISO 75-2/B |
| Melting temperature | |||
| DSC | 223 | ℃ | ISO 3146 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 100 to 120 | °C | |
| Drying time | 4.0 | hr | |
| Recommended maximum moisture content | 0.040 | % | |
| Processing (melt) temperature | 250 to 275 | °C | |
| Mold temperature | 40 to 70 | °C | |
| Injection pressure | 3.50 to 12.5 | MPa | |
| Injection speed | Fast | ||
| Back pressure | < 1.00 | MPa | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |