| About |
|---|
| Ultramid 1503-2 NF2004 is a 33% glass reinforced, heat stabilized injection molding PA6/6.&& |
| Product Description | |
|---|---|
| Supplier | BASF |
| Generic | PA66 |
| Material Status | Commercial: Active |
| Features | Heat Stabilized |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.40 | g/cm³ | ASTM D792 |
| Density | 1.40 | g/cm³ | ISO 1183 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.30 | % | |
| Water absorption rate | |||
| Saturation, 23 ℃ | 5.7 | % | ISO 62 |
| saturated | 5.7 | % | ASTM D570 |
| Equilibrium, 23 ℃, 50% RH | 1.7 | % | ISO 62 |
| Balance, 50% RH | 1.7 | % | ASTM D570 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 23℃ | 10800 | MPa | ISO 527-2 |
| tensile strength | |||
| Fracture, 23 ℃ | 210 | MPa | ISO 527-2 |
| Fracture, 23 ℃ | 193 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 23 ℃ | 3.0 | % | ASTM D638 |
| Fracture, 23 ℃ | 3.0 | % | ISO 527-2 |
| Bending modulus | |||
| 23℃ | 9900 | MPa | ISO 178 |
| 23℃ | 8280 | MPa | ASTM D790 |
| bending strength | |||
| 23℃ | 276 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30℃ | 11 | kJ/m² | ISO 179 |
| 23℃ | 12 | kJ/m² | ISO 179 |
| Charpy Unnotch Impact strength | ISO 179 | ||
| -30℃ | 75 | kJ/m² | ISO 179 |
| 23℃ | 90 | kJ/m² | ISO 179 |
| Impact strength of cantilever beam notch | |||
| 23℃ | 11 | kJ/m² | ISO 180 |
| 23℃ | 120 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 255 | ℃ | ISO 75-2/A |
| 1.8 MPa, unannealed | 252 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed | 264 | ℃ | ISO 75-2/B |
| 0.45 MPa, unannealed | 297 | ℃ | ASTM D648 |
| Melting peak temperature | 260 | ℃ | ASTM D3418 |
| Melting temperature | |||
| DSC | 260 | ℃ | ISO 3146 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 60 | °C | |
| Drying time | 1.0 to 2.0 | hr | |
| Recommended maximum moisture content | 0.040 to 0.20 | % | |
| Processing (melt) temperature | 288 to 305 | °C | |
| Mold temperature | 60 to 100 | °C | |
| Injection pressure | 3.50 to 12.5 | MPa | |
| Injection speed | Fast | ||
| Back pressure | 0.00 to 0.350 | MPa | |
| Screw speed | 40 to 80 | rpm | |
| Screw compression ratio | 3.0:1.0 to 4.0:1.0 | ||
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |