| About |
|---|
| Product Description | |
|---|---|
| Supplier | BASF |
| Generic | PA66 |
| Material Status | Commercial: Active |
| Features | Heat Stabilized |
| Availabilitys | Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Forming shrinkage | |||
| MD | 0.28 | % | ISO 294-4 |
| TD | 0.98 | % | ISO 294-4 |
| Water absorption | |||
| 24 hours in the water at 23 ℃ | 0.9 | % | ISO 62 |
| Equilibrium equilibrium, 23 ℃ | 5.5 | % | ISO 62 |
| Moisture absorption | |||
| Parallel, 23 ℃, 50% humidity, r. h | 1.6 | % | ISO 62 |
| Density | |||
| 1390 | kg/m³ | ISO 1183 | |
| ASTM | 1.39 | g/cm³ | ASTM D792 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| Dry | 11300 | MPa | ISO 527-2 |
| Wet Cond | 7800 | MPa | ISO 527-2 |
| Tensile strength | |||
| 50 mm/min, dry, yield yld | 200 | MPa | ISO 527-2 |
| 2 in/min, dry, yield yld | 200 | MPa | ASTM D638 |
| Dry, broken | 205 | MPa | ISO 527-2 |
| Wet cond, fracture | 145 | MPa | ISO 527-2 |
| Tensile strain | |||
| Break, dry dry | 3 | % | ISO 527-2 |
| Break, wet cond | 5 | % | ISO 527-2 |
| Elongation at break | |||
| 2 in/min, dry | 3.5 | % | ASTM D638 |
| 9700 | MPa | ISO 178 | |
| ASTM | 10300 | MPa | ASTM D790 |
| 270 | MPa | ISO 178 | |
| ASTM, dry | 300 | MPa | ASTM D790 |
| ASTM, Wet Cond | 17 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy notched impact strength | |||
| Dry | 13 | kJ/m² | ISO 179/1eA |
| Wet Cond | 95 | kJ/m² | ISO 179/1eA |
| Charpy impact strength of simply supported beams | |||
| Dry | 85 | KJ/m² | ISO 179/1eU |
| Izod notched impact strength | |||
| Dry | 15 | KJ/m² | ISO 180/1A |
| Wet Cond | 20 | J/m | ASTM D256 |
| Dry | 130 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature HDT | |||
| 1.80 MPa | 250 | ℃ | ISO 75-1/-2 |
| 1.82 MPa | 250 | ℃ | ASTM D648 |
| Melting temperature | 262 | ℃ | ISO 11357-3 |
| ELECTRICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Dry | 6E14 | ohm | IEC 62631-3-2 |
| Wet Cond | 1E12 | ohm | IEC 62631-3-1 |
| Dry | 1E13 | ohm·m | IEC 60243-1 |
| Wet Cond | 1E11 | ohm·m | IEC 60243-1 |
| Electric strength | |||
| D=2 mm, dry | 34 | kV/mm | IEC 62631-2-1 |
| D=2 mm, moist cond | 29 | kV/mm | IEC 62631-2-1 |
| Dissipation factor | |||
| Dry | 0.01 | E-4 | IEC 60112 |
| Wet Cond | 0.11 | E-4 | IEC 60112 |
| Compared tracking index | |||
| Test liquid A, dry | 450 | IEC 60112 | |
| Test liquid A, wet cond | 425 | IEC 60112 | |
| Test liquid A, dry | 350 | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 0.8 mm | HB | calss | IEC 60695-11-10 |
| Glow Wire Flammability Index | |||
| 1.6 mm | 700 | ℃ | IEC 60695-2-12 |
| Oxygen index | 23 | % | ISO 4589-2 |
| Process Conditions | |||
|---|---|---|---|
| Injection | Nominal value | Unit | Test method |
| Drying temperature | 80.0 to 100 | °C | |
| Recommended maximum water content | 0.20 | % | |
| Rear Temperature Zone 1 | 270 to 275 | °C | |
| Middle Temperature Zone 2 | 275 to 285 | °C | |
| Front Temperature Zone 3 | 285 to 295 | °C | |
| Mold Temperature | 80.0 to 100 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |