| About |
|---|
| Product Description | |
|---|---|
| Supplier | BASF |
| Generic | PA66 |
| Material Status | Commercial: Active |
| Features | High impact resistance,Quick molding cycle,Good surface appearance |
| Availabilitys | Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Water absorption | |||
| 23 ℃, 24 hours in the water | 1.1 | % | ISO 62 |
| Balance, 23 ℃, 50% humidity | 2.4 | % | ISO 62 |
| Density | 1100 | kg/m³ | ISO 1183 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| Dry | 2500 | MPa | ISO 527-2 |
| Wet Cond | 1100 | MPa | ISO 527-2 |
| Tensile strength | |||
| 80 | MPa | ISO 527-2 | |
| 40 | MPa | ISO 527-2 | |
| Break, wet cond, 2 in/min | 62 | MPa | ASTM D638 |
| Break, dry dry | 80 | MPa | ISO 527-2 |
| Break, wet cond | 40 | MPa | ISO 527-2 |
| Tensile Strain | |||
| Yield yld, dry dry dry | 10 | % | ISO 527-2 |
| Yield yld, wet cond | 16 | % | ISO 527-2 |
| Break, dry dry | 25 | % | ISO 527-2 |
| Break, wet cond | >250 | % | ISO 527-2 |
| Elongation at break | |||
| Dry, 2 in/min | 30 | % | ASTM D638 |
| 2200 | MPa | ISO 178 | |
| Wet Cond | 1050 | MPa | ISO 178 |
| Flexural strength | |||
| Dry | 90 | MPa | ISO 178 |
| Wet Cond | 40 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy notched impact strength | |||
| Dry | 18 | kJ/m² | ISO 179/1eA |
| Wet Cond | 90 | kJ/m² | ISO 179/1eA |
| Izod notched impact strength | 250 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature HDT | |||
| 1.8 MPa | 92 | ℃ | ISO 75-1/-2 |
| 1.82 MPa | 70 | ℃ | ASTM D648 |
| 0.45 MPa | 210 | ℃ | ISO 75-1/-2 |
| Melting temperature | 262 | ℃ | ISO 11357-3 |
| ELECTRICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | |||
| Dry | 1E15 | ohm | IEC 62631-3-2 |
| Wet Cond | 1E15 | ohm | IEC 62631-3-2 |
| Volume resistivity | |||
| Dry | 1E13 | ohm·m | IEC 62631-3-1 |
| Wet Cond | 1E13 | ohm·m | IEC 62631-3-1 |
| Dry | 30 | kV/mm | IEC 60243-1 |
| Wet Cond | 16 | kV/mm | IEC 60243-1 |
| Compared tracking index | |||
| Dry, test solution A | 550 | IEC 60112 | |
| 470 | |||
| Relative permittivity | |||
| Dry | 3.2 | IEC 62631-2-1 | |
| Wet Cond | 3.2 | IEC 62631-2-1 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame Class Rating | |||
| 3.2 mm | HB | calss | IEC 60695-11-10 |
| Process Conditions | |||
|---|---|---|---|
| Injection | Nominal value | Unit | Test method |
| Drying Temperature | 80.0 | °C | |
| Suggested Maximum Moisture Content | 0.20 | % | |
| Rear Temperature Zone 1 | 265 to 270 | °C | |
| Middle Temperature Zone 2 | 270 to 280 | °C | |
| Front Temperature Zone 3 | 280 to 290 | °C | |
| Mold Temperature | 70.0 to 100 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |