Ultramid® 8235G HS BK-102

About
Ultramid 8235G HS BK-102 is a heat stabilized, pigmented black, 50% glass fiber reinforced PA6 injection molding compound offering excellent level of strength, stiffness, high temperature performance and dimensional stability. Its resistance to creep under load is excellent. It is available in natural, black, weather resistance and pigmented versions. Applications Ultramid 8235G HS BK-102 is generally recommended for applications such as power tool housings, cattle ear taggers, luggage frames, fans and pressure regulator housings.&&

About

Ultramid 8235G HS BK-102 is a heat stabilized, pigmented black, 50% glass fiber reinforced PA6 injection molding compound offering excellent level of strength, stiffness, high temperature performance and dimensional stability. Its resistance to creep under load is excellent. It is available in natural, black, weather resistance and pigmented versions. Applications Ultramid 8235G HS BK-102 is generally recommended for applications such as power tool housings, cattle ear taggers, luggage frames, fans and pressure regulator housings.&&

Product Description
Supplier	BASF
Generic	PA6
Material Status	Commercial: Active
Features	Good Rigidity,Good flexibility,Good Dimensional Stability,High Heat Resistance,Heat Stabilized,HB
Availabilitys	North America
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.56	g/cm³	ASTM D792
Density	1.56	g/cm³	ISO 1183
Shrinkage rate
MD：3.2 mm	0.20	%
Water absorption rate
Saturation, 23 ℃	4.8	%	ISO 62
saturated	4.8	%	ASTM D570
Equilibrium, 23 ℃, 50% RH	1.4	%	ISO 62
Balance, 50% RH	1.4	%	ASTM D570

MECHANICAL	Nominal value	Unit	Test method
Tensile modulus
23℃	15800	MPa	ISO 527-2
tensile strength
Fracture, 23 ℃	210	MPa	ASTM D638
Fracture, 23 ℃	210	MPa	ISO 527-2
Tensile strain
Fracture, 23 ℃	2.0	%	ISO 527-2
Fracture, 23 ℃	2.0	%	ASTM D638
Bending modulus
23℃	13200	MPa	ISO 178
23℃	14700	MPa	ASTM D790
bending strength
23℃	300	MPa	ISO 178

IMPACT	Nominal value	Unit	Test method
Charpy Notched Impact Strength
23℃	15	kJ/m²	ISO 179
Charpy Unnotch Impact strength
23℃	70	kJ/m²	ISO 179
Impact strength of cantilever beam notch			ISO 180
23℃	140	J/m	ASTM D256
-40℃	12	kJ/m²	ISO 180
23℃	15	kJ/m²	ISO 180

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
1.8 MPa, unannealed	210	℃	ISO 75-2/A
0.45 MPa, unannealed	220	℃	ISO 75-2/B
Melting peak temperature	220	℃	ASTM D3418
Melting temperature
DSC	220	℃	ISO 3146
0.75 mm	65.0	℃	UL 746
1.7 mm	130	℃	UL 746
3.0 mm	130	℃	UL 746
Relative temperature index
Electrical performance			UL 746
Strength mechanical performance			UL 746
Impact mechanical performance			UL 746
0.75 mm	65.0	℃	UL 746
1.7 mm	105	℃	UL 746
3.0 mm	105	℃	UL 746
0.75 mm	65.0	℃	UL 746
1.7 mm	130	℃	UL 746
3.0 mm	130	℃	UL 746

Electrical performance	Nominal value	Unit	Test method
Volume resistivity	> 1.0E+13	ohms·cm	IEC 60093
1.50 mm	> 1.0E+13	ohms·cm	ASTM D257

FLAME CHARACTERISTICS	Nominal value	Test method
Flame retardant level		UL 94
0.75 mm	HB	UL 94
1.70 mm	HB	UL 94
3.00 mm	HB	UL 94

Process Conditions
injection	Nominal value	Unit	Test method
Drying temperature	80	°C
Drying time	2.0 to 4.0	hr
Recommended maximum moisture content	0.060	%
Processing (melt) temperature	280 to 305	°C
Mold temperature	80 to 95	°C
Injection pressure	3.50 to 12.5	MPa
Injection speed	Fast

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.