Ultramid® 8333G HI HS BK-106

About
Ultramid 8333G HI HS BK-106 is a 33% glass reinforced, impact modified PA6 injection molding compound pigmented black developed for applications requiring improved dry as molded toughness in combination with a balance of strength, stiffness and excellent moldability/surface aesthetics. Applications Ultramid 8333G HI HS BK-106 is generally recommended for application such as front wheel chair wheels, bicycle wheels, power tool housings, chain saw housings, clips and fasteners, hose clamps and window hardware.&&

About

Ultramid 8333G HI HS BK-106 is a 33% glass reinforced, impact modified PA6 injection molding compound pigmented black developed for applications requiring improved dry as molded toughness in combination with a balance of strength, stiffness and excellent moldability/surface aesthetics. Applications Ultramid 8333G HI HS BK-106 is generally recommended for application such as front wheel chair wheels, bicycle wheels, power tool housings, chain saw housings, clips and fasteners, hose clamps and window hardware.&&

Product Description
Supplier	BASF
Generic	PA6
Material Status	Commercial: Active
Features	Good Rigidity,Good surface appearance,High impact resistance
Availabilitys	North America
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.36	g/cm³	ASTM D792
Density	1.36	g/cm³	ISO 1183
Shrinkage rate
MD：3.2 mm	0.30	%
Water absorption rate
Saturation, 23 ℃	5.5	%	ISO 62
saturated	5.5	%	ASTM D570
Equilibrium, 23 ℃, 50% RH	1.5	%	ISO 62
Balance, 50% RH	1.5	%	ASTM D570
24hr	0.90	%	ASTM D570
23℃，24hr	0.90	%	ISO 62

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch
23℃	180	J/m	ASTM D256
23℃	18	kJ/m²	ISO 180

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
1.8 MPa, unannealed	208	℃	ASTM D648
Melting peak temperature	220	℃	ASTM D3418
Melting temperature
DSC	220	℃	ISO 3146

MECHANICAL	Nominal value	Unit	Test method
tensile strength
Fracture, 23 ℃	145	MPa	ASTM D638
Fracture, 23 ℃	145	MPa	ISO 527-2
Tensile strain
Fracture, 23 ℃	2.5	%	ISO 527-2
Fracture, 23 ℃	2.5	%	ASTM D638
Bending modulus
23℃	7910	MPa	ISO 178
23℃	7990	MPa	ASTM D790
bending strength
23℃	232	MPa	ASTM D790
Rockwell hardness
R-level	121		ASTM D785

Process Conditions
injection	Nominal value	Unit	Test method
Drying temperature	80	°C
Drying time	2.0 to 4.0	hr
Recommended maximum moisture content	0.080	%
Barrel rear temperature	245 to 275	°C
Barrel middle temperature	260 to 285	°C
Barrel front temperature	270 to 295	°C
Nozzle temperature	270 to 295	°C
Processing (melt) temperature	270 to 295	°C
Mold temperature	80 to 95	°C
Injection pressure	3.50 to 12.5	MPa
Injection speed	Fast

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.