Ultramid® A 20 V35 NATURAL

About
TECHNYL® A 20 V35 Natural is a Red Phosphorous flame retardant polyamide 66, reinforced with 35% of glass fiber, heat stabilized, for injection moulding. This grade provides robust UL 94 V-0 and a full UL yellow card while offering good mechanical properties. This grade is suitable for moulding insulating parts for electrical devices, and more generally for thin parts under stress.&&

Product Description
Supplier	BASF
Generic	PA66
Material Status	Commercial: Negative
Availabilitys	Europe,Africa & Middle East ,Asia Pacific
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Water absorption
24 h，23℃	0.6	%	ISO 62
Equilibrium equilibrium, 24 hours, 23 ℃	1.7	%	ISO 62
Density	1460	kg/m³	ISO 1183

MECHANICAL	Nominal value	Unit	Test method
Tensile modulus
Dry	12500	MPa	ISO 527-2
Wet Cond	8200	MPa	ISO 527-2
Tensile Strength
Dry	175	MPa	ISO 527-2
Wet Cond	110	MPa	ISO 527-2
Tensile Strain
	2.1	%	ISO 527-2
Wet Cond	3.2	%	ISO 527-2
Flexural modulus
Dry	11000	MPa	ISO 178
Wet Cond	7500	MPa	ISO 178
Flexural strength
Dry	260	MPa	ISO 178
Wet Cond	200	MPa	ISO 178

IMPACT	Nominal value	Unit	Test method

-30 ℃, dry	8	kJ/m²	ISO 179/1eA
23 ℃, dry	10	kJ/m²	ISO 179/1eA
23 ℃, moist cond	12	kJ/m²	ISO 179/1eA

-30 ℃, dry	55	KJ/m²	ISO 179-1
23 ℃, dry	60	KJ/m²	ISO 179-1
23 ℃, moist cond	70	KJ/m²	ISO 179-1
Izod notched impact strength
23 ℃, dry	10	KJ/m²	ISO 180/1A
23 ℃, moist cond	12	KJ/m²	ISO 180/1A

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature HDT
1.80MPa	244	℃	ISO 75-1/-2
Melting temperature	263	℃	ISO 11357-1/-3

FLAME CHARACTERISTICS	Nominal value	Unit	Test method
Flame retardant level
1.6 mm	V-0	calss	UL 94
0.8 mm	V-0	calss	UL 94
3.2 mm	V-0	calss	UL 94
Glow Wire Flammability Index
0.8mm	960	℃	IEC 60695-2-12
1.6mm	960	℃	IEC 60695-2-12
3.2mm	960	℃	IEC 60695-2-12

1.6mm	725	℃	IEC 60695-2-13
	31	%	ISO 4589-1/-2

ELECTRICAL	Nominal value	Unit	Test method
Surface resistivity
	1E14	ohm	IEC 62631-3-2
Wet Cond	1E13	ohm	IEC 62631-3-2
Volume resistivity
Dry	1E13	ohm·m	IEC 62631-3-1
Wet Cond	1E13	ohm·m	IEC 62631-3-1

Dry, d=0.8 mm	32	KV/mm	IEC 60243-1

Dry	3.4		IEC 62631-2-1
Wet Cond	4		IEC 62631-2-1
Dissipation factor
Dry	0.02	E-4	IEC 62631-2-1
Wet Cond	0.05	E-4	IEC 62631-2-1
Compared tracking index
Test fluid A	400		IEC 60112

Process Conditions
Injection molding	Nominal value	Unit	Test method
Drying temperature	80	°C
Recommended maximum water content	0.20	%
Injection molding cylinder temperature 1	265 to 275	°C
Injection molding cylinder temperature 2	270 to 280	°C
Injection molding cylinder temperature 3	280 to 290	°C
Mold temperature	60 to 90	°C

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.