| About |
|---|
| Product Description | |
|---|---|
| Supplier | BASF |
| Generic | PA66 |
| Material Status | Commercial: Active |
| Features | Heat Stabilized,HB |
| Availabilitys | Europe,North America,Africa & Middle East ,Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.36 | g/cm³ | ISO 1183/A |
| Water Absorption | |||
| Equilibrium, 23 ℃, 50% RH | 1.7 | % | ISO 62 |
| 23℃，24hr | 0.80 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile Modulus | |||
| 23℃ | 10000 | MPa | ISO 527-2/1A |
| Tensile Strength | |||
| Fracture, 23 ℃ | 190 | MPa | ISO 527-2/1A |
| Tensile Strain | |||
| Fracture, 23 ℃ | 3.0 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23℃ | 9000 | MPa | ISO 178 |
| 23℃ | 9000 | MPa | ASTM D790 |
| Flexural Strength | |||
| 23℃ | 290 | MPa | ASTM D790 |
| 23℃ | 280 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 11 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | |||
| 23℃ | 75 | kJ/m² | ISO 179/1eU |
| Izod Notched Impact strength | |||
| 23℃ | 10 | kJ/m² | ISO 180 |
| 23℃ | 120 | J/m | ASTM D256 |
| Izod Unnotched Impact strength of cantilever beam | |||
| 23℃ | 60 | kJ/m² | ISO 180/1U |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature HDT | |||
| 1.8 MPa, unannealed | 255 | ℃ | ISO 75-2/Af |
| 0.45 MPa, unannealed | 260 | ℃ | ISO 75-2/Bf |
| Melting temperature | 262 | ℃ | ISO 11357-3 |
| ELECTRICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface Resistivity | 6.0E+15 | ohms | IEC 60093 |
| Volume Resistance | 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength | |||
| 2 mm | 34 | kV/mm | IEC 60243-1 |
| Relative permittivity | 3.70 | IEC 60250 | |
| Dissipation Factor | 0.010 | IEC 60250 | |
| Compared Tracking Index | IEC 60112 | ||
| Solution A | 600 | V | IEC 60112 |
| Solution B | 500 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame Class Rating | UL 94 | ||
| 1.60 mm | HB | UL 94 | |
| 3.20 mm | HB | UL 94 | |
| Glow Wire Flammability Index GWFI | |||
| 1.6 mm | 700 | ℃ | IEC 60695-2-12 |
| Oxygen Index | 23 | % | ISO 4589-2 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| European Railway Certification | EN 45545-2 | ||
| R22 | NC | EN 45545-2 | |
| R23 | NC | EN 45545-2 |
| Process Conditions | |||
|---|---|---|---|
| Injection Molding | Nominal value | Unit | Test method |
| Drying Temperature | 80 | °C | |
| Maximum Moisture Content | 0.20 | % | |
| Rear Temperature Zone 1 | 270 to 280 | °C | |
| Middle Temperature Zone 2 | 275 to 285 | °C | |
| Front Temperature Zone 3 | 280 to 290 | °C | |
| Mold Temperature | 70 to 100 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |