Ultramid® A 246M BLACK 21 N

About
TECHNYL® A 246M Black 21 N is an unfilled polyamide 6.6, impact modified, for injection moulding. This grade offers an excellent impact resistance, even at low temperature.&&

Product Description
Supplier	BASF
Generic	PA66
Material Status	Commercial: Active
Features	HB,low-temperature impact resistance,High impact resistance
Availabilitys	North America,Africa & Middle East ,Europe
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Molding shrinkage
Parallel	1.6	%	ISO 294-4
Normal	1.3	%	ISO 294-4
Water Absorption
24 h，23℃	1.1	%	ISO 62
Density	1080	kg/m³	ISO 1183

MECHANICAL	Nominal value	Unit	Test method
Tensile Modulus
Dry	1900	MPa	ISO 527
Wet Cond	600	MPa	ISO 527
Tensile Strength
Yield yld, 50 mm/min, dry dry	47	MPa	ISO 527-2
Yield yld, 50 mm/min, wet cond	42	MPa	ISO 527-2
Yield yld, 2 in/min	50	MPa	ASTM D638
Broken BRK, dry dry	44	MPa	ISO 527-2
Broken BRK, wet Cond	35	MPa	ISO 527-2
Tensile Strain
Yield yld, 50 mm/min, dry dry	20	%	ISO 527
Yield yld, 50 mm/min, wet cond	210	%	ISO 527
Elongation at Break	80	%	ASTM D638
Flexural Modulus
Dry	1800	MPa	ISO 178
Wet Cond	700	MPa	ISO 178
Dry	1800	MPa	ASTM D790
Flexural Strength
Dry	70	MPa	ISO 178
Wet Cond	27	MPa	ISO 178
Dry	70	MPa	ASTM D790

IMPACT	Nominal value	Unit	Test method
Charpy Notched Impact Strength
Dry, 23 ℃	97	kJ/m²	ISO 179/1eA
Wet Cond, 23 ℃	100	kJ/m²	ISO 179/1eA
Charpy Unnotch Impact strength
-30℃	16	kJ/m²	ISO 179/1eU
Izod Notched Impact strength
Dry, -30 ℃	22	KJ/m²	ISO 180/1A
Dry, 23 ℃	60	KJ/m²	ISO 180/1A
Wet Cond, 23 ℃	80	KJ/m²	ISO 180/1A
Dry, 23 ℃	100	J/m	ISO 180/1A
Wet Cond, 23 ℃	120	J/m	ASTM D256

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature HDT
0.45 MPa	200	℃	ISO 75-1/-2
1.80 MPa	65	℃	ISO 75-1/-2
1.82 MPa	63	℃	ISO 75-1/-2
Melting temperature	263	℃	ISO 11357-3

ELECTRICAL	Nominal value	Unit	Test method
Surface Resistivity
Dry	1E15	ohm	IEC 62631-3-2
Wet Cond	1E14	ohm	IEC 62631-3-2
Volume Resistance
Dry	1E13	ohm·m	IEC 62631-3-1
Wet Cond	1E13	ohm·m	IEC 62631-3-1
Electric strength
Dry	35	kV/mm	IEC 60243-1
Wet Cond	22	kV/mm	IEC 60243-1
Relative permittivity
	3.5	E-4	IEC 62631-2-1
	4	E-4	IEC 62631-2-1
Dissipation Factor	0.033
Compared Tracking Index
Dry	575		IEC 60112
Wet Cond	600		IEC 60112
Dry	450		IEC 60112

FLAME CHARACTERISTICS	Nominal value	Unit	Test method
Flame Class Rating
1.6 mm	HB	calss	IEC 60695-11-10

Process Conditions
Injection Molding	Nominal value	Unit	Test method
Drying Temperature	80	℃
Maximum Moisture Content	0.2	%
Rear Temperature Zone 1	265-275	℃
Middle Temperature Zone 2	270-280	℃
Front Temperature Zone 3	280-285	℃
Mold Temperature	60-80	℃

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.