Ultramid® A 30H1 V30 NATURAL

About

Product Description
Supplier	BASF
Generic	PA66
Material Status	Commercial: Active
Features	Excellent Processability,Flame Characteristics,Good Electrical Properties
Availabilitys	Latin America,North America,Europe,Asia Pacific,Africa & Middle East
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method

Parallel	0.36	%	ISO 294-4
Vertical normal	1.00	%	ISO 294-4
Water absorption
Equilibrium equilibrium, 23 ℃	0.8	%	ISO 62
Density	1570	kg/m³	ISO 1183

MECHANICAL	Nominal value	Unit	Test method

Dry	10000	MPa	ISO 527-2
Wet Cond	7000	MPa	ISO 527-2

Break, dry dry	130	MPa	ISO 527-2
Break, wet cond	95	MPa	ISO 527-2
Break, dry dry	140	MPa	ASTM D638
Tensile Strain
Break, dry dry	2.2	%	ISO 527-2
Break, wet cond	3.5	%	ISO 527-2
Tensile elongation at break
2 in/min	2.5	%	ASTM D638
Flexural modulus
Dry	9500	MPa	ISO 178
Wet Cond	7000	MPa	ISO 178
Dry	9500	MPa	ASTM D790
Flexural strength
Dry	200	MPa	ISO 178
Wet Cond	160	MPa	ISO 178
Dry	200	MPa	ASTM D790

IMPACT	Nominal value	Unit	Test method
Charpy notched impact strength
	9.5	kJ/m²	ISO 179/1eA
Wet Cond	12	kJ/m²	ISO 179/1eA
Charpy impact strength of simply supported beams
Dry	42	KJ/m²	ISO 179-1eU
Wet Cond	50	KJ/m²	ISO 179-1eU
Izod notched impact strength
Dry	10	KJ/m²	ISO 180/1A
Wet Cond	13	KJ/m²	ISO 180/1A
Dry	120	J/m	ASTM D256

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature HDT
1.80 MPa	226	℃	ISO 75-1/-2
1.82 MPa	227	℃	ASTM D648
Melting temperature	263	℃	ISO 11357-3

ELECTRICAL	Nominal value	Unit	Test method
Surface resistivity	1E14	ohm	IEC 62631-3-2
Volume resistivity	1E13	ohm·m	IEC 62631-3-1
Electrical strength
D=0.8 mm, dry	42	KV/mm	IEC 60243-1
D=0.8 mm, wet cond	40	KV/mm	IEC 60243-1
Relative permittivity
Dry	3.3		IEC 62631-2-1
Wet Cond	3.6		IEC 62631-2-1
Dissipation factor
Dry	0.01	E-4	IEC 62631-2-1
Wet Cond	0.05	E-4	IEC 62631-2-1
Compared tracking index
	450		IEC 60112
Test solution A, moisten cond	600		IEC 60112
Test solution B, dry dry	400		IEC 60112
Test fluid B, wet cond	500		IEC 60112

FLAME CHARACTERISTICS	Nominal value	Unit	Test method
Flame retardant level
1.6 mm	V-0	calss	IEC 60695-11-10
0.8 mm	V-0	calss	IEC 60695-11-10
3.2 mm	V-0	calss	UL 94,IEC 60695

0.8 mm	960	℃	IEC 60695-2-12
1.6 mm	960	℃	IEC 60695-2-12
3.2 mm	960	℃	IEC 60695-2-12
Glow Wire Ignition Temperature
0.8 mm	800	℃	IEC 60695-2-13
1.6 mm	825	℃	IEC 60695-2-13
	31	%	ISO 4589-2

Process Conditions
Injection	Nominal value	Unit	Test method
Drying temperature	80.0	°C
Recommended maximum water content	0.20	%
Injection molding cylinder temperature 1	270 to 280	°C
Injection molding cylinder temperature 2	275 to 285	°C
Injection molding cylinder temperature 3	280 to 290	°C
Mold temperature	70.0 to 100	°C

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.