Ultramid® A 60G1 V30 NATURAL

About
TECHNYL® A 60G1 V30 Natural is a polyamide 66 based on a non-halogenated flame retardant system, reinforced with 30% of glass fiber, heat stabilized, for injection moulding. This grade offers excellent flame retardancy properties (UL 94, 5VA, GWIT) combined with excellent processing, mechanical and electrical performance. It can withstand temperatures of 160°C for over 6000 hours and has a UL F1 rating for weatherability resistance&&

About

TECHNYL® A 60G1 V30 Natural is a polyamide 66 based on a non-halogenated flame retardant system, reinforced with 30% of glass fiber, heat stabilized, for injection moulding. This grade offers excellent flame retardancy properties (UL 94, 5VA, GWIT) combined with excellent processing, mechanical and electrical performance. It can withstand temperatures of 160°C for over 6000 hours and has a UL F1 rating for weatherability resistance&&

Product Description
Supplier	DOMO
Generic	PA66
Material Status	Commercial: Active
Features	V-0
Availabilitys	Africa & Middle East ,North America,Latin America,Asia Pacific,Europe
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.46	g/cm³	ISO 1183/A
Water absorption rate
Saturation, 23 ℃	4.3	%	ISO 62
Equilibrium, 23 ℃, 50% RH	1.8	%	ISO 62
23℃，24hr	0.73	%	ISO 62
Weathering resistance	f1		UL 746C

MECHANICAL	Nominal value	Unit	Test method
Tensile modulus
23℃	11700	MPa	ISO 527-2/1A
tensile strength
Fracture, 23 ℃	140	MPa	ASTM D638
Fracture, 23 ℃	150	MPa	ISO 527-2/1A
Tensile strain
Fracture, 23 ℃	3.5	%	ASTM D638
Fracture, 23 ℃	2.3	%	ISO 527-2
Bending modulus
23℃	11000	MPa	ISO 178
23℃	11000	MPa	ASTM D790
bending strength
23℃	225	MPa	ASTM D790
23℃	255	MPa	ISO 178

IMPACT	Nominal value	Unit	Test method
Charpy Notched Impact Strength			ISO 179/1eA
-30℃	9.5	kJ/m²	ISO 179/1eA
23℃	10	kJ/m²	ISO 179/1eA
Charpy Unnotch Impact strength			ISO 179/1eU
-30℃	60	kJ/m²	ISO 179/1eU
23℃	60	kJ/m²	ISO 179/1eU
Impact strength of cantilever beam notch
23℃	85	J/m	ASTM D256

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
1.8 MPa, unannealed	245	℃	ISO 75-2/Af
Melting temperature	263	℃	ISO 11357-3

Electrical performance	Nominal value	Unit	Test method
Volume resistivity	6.0E+14	ohms·cm	IEC 60093
Dielectric strength
0.8 mm	38	kV/mm	IEC 60243-1
Compared to the leakage tracing index
Solution A	600	V	IEC 60112

FLAME CHARACTERISTICS	Nominal value	Unit	Test method
Flame retardant level			UL 94
0.80 mm	V-0		UL 94
1.60 mm	V-0 5VA		UL 94
3.20 mm	V-0 5VA		UL 94
Glowing wire flammability index			IEC 60695-2-12
0.80 mm	960	℃	IEC 60695-2-12
1.6 mm	960	℃	IEC 60695-2-12
3.2 mm	960	℃	IEC 60695-2-12
Igniting temperature of the hot wire
0.8 mm	775	℃	IEC 60695-2-13
Extreme oxygen index	33	%	ISO 4589-2
French Fire Index	F3		NF F16-101
French Smoke Index	I3		NF F16-101

Supplementary information	Nominal value	Test method
European Railway Certification		EN 45545-2
R22	HL3	EN 45545-2
R23	HL3	EN 45545-2

Process Conditions
Injection	Nominal value	Unit	Test method
drying temperature	80	°C
Recommended maximum moisture content	0.20	%
Temperature at the rear of the barrel	265 to 275	°C
Temperature in the middle of the barrel	265 to 275	°C
Front temperature of material barrel	270 to 280	°C
Mold temperature	60 to 90	°C

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.