| Ultramid® A3HG6 它对弱酸性介质的抗性使其优于PA 6和PA 66。 |
| Product Description | |
|---|---|
| Supplier | BASF |
| Generic | PA66 |
| Material Status | Commercial: Active |
| Availabilitys | Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.34 | g/cm³ | ISO 1183 |
| Water absorption rate | |||
| saturated | 3.8 | % | ISO 62 |
| balance | 1.3 | % | ISO 62 |
| Viscosity measurement | 150 | cm3/g | ISO 307 |
| Melt Flow Rate | |||
| 275℃，5.0kg | 26.86 | g/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| fracture | 125 | MPa | ISO 527-1-2 |
| Tensile strain | |||
| yield | 5 | % | ISO 527-1/2 |
| Elastic modulus | 7.2 | GPa | ISO 527-1/-2 |
| bending strength | |||
| 23℃ | 200 | MPa | ISO 178 |
| Bending modulus | |||
| 23℃ | 6700 | MPa | ISO 178 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Linear coefficient of thermal expansion | |||
| MD | 0.004 | 1/℃ | ISO 2577 |
| TD | 0.01 | 1/℃ | ISO 2577 |
| melting point | 260 | ℃ | ISO 11357-1/-3 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 9 | J/cm² | ISO 179/1eU | |
| 1.4 | J/cm² | ISO 179/1eA |
| Process Conditions | |||
|---|---|---|---|
| injection molding | Nominal value | Unit | Test method |
| Melting temperature | 270-290 | °C | |
| Mold temperature | 80-90 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |