| About |
|---|
| Very easy flowing injection moulding grade for rapid production of thin-walled technical parts (eg housings and small components)&& |
| Product Description | |
|---|---|
| Supplier | BASF |
| Generic | PA66 |
| Material Status | Commercial: Active |
| Features | Good liquidity,Quick molding cycle,Grease resistance |
| Availabilitys | Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Melt Volume Rate | 135 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| Restricted 4 | 0.65 | % | |
| Density | 1.140 | g/cm³ | ISO 1183 |
| Viscosity value | 150 | g/cm³ | ISO 307, 1157, 1628 |
| 2.5-3.1 | % | ISO 62 | |
| Saturation, 23 ℃ | 8-9 | % | ISO 62 |
| handle | Nominal value | Unit | Test method |
|---|---|---|---|
| melting point | 260 | °C | ISO 11357-1/-3 |
| temperature | 275 | °C | ISO 1133 |
| load | 5 | kg | ISO 1133 |
| Melting temperature | |||
| Injection molding/extrusion | 280 – 300 | ℃ | |
| Mold temperature | 40 – 80 | °C | – |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 1.6 mm | V-2 | – | UL 94 |
| Automotive materials | |||
| Thickness>=1mm | + | – | – |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 3500/1600 | MPa | ISO 527-1-2 |
| Yield stress | 95/60 | MPa | ISO 527-1/-2 |
| tensile strength | |||
| fracture | 15/>50 | % | ISO 527-1/-2 |
| yield | 4.3/20 | % | ISO 527-1/-2 |
| Bending modulus | 3200/- | MPa | ISO 178 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa | 75 | ℃ | ISO 75-1/2 |
| Hot deformation temperature | |||
| 0.45 MPa | 220 | ℃ | ISO 75-1/2 |
| MD 23-80°C | 0.7-1 | E-4/°C | ISO 11359-1/-2 |
| Thermal conductivity | 0.33 | W/(mK) | DIN 52612-1 |
| Specific heat capacity | 1700 | J/(kg*K) | – |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| 1 MHz | 3.2/5 | IEC 60250 | |
| Dissipation coefficient | |||
| 1MHz | 250/2000 | E-4 | IEC 60250 |
| Volume resistivity | 1E13/1E10 | Ohm*m | IEC 60093 |
| Surface resistivity | 1E+10 | ohms | IEC 60093 |
| Compared to the leakage tracing index | |||
| Solution A | 600 | IEC 60112 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 4/15 | kJ/m² | ISO 179/1eU |
| 23℃ | N/N | kJ/m² | ISO 179/1eU |
| Impact strength of cantilever beam notch | |||
| -30℃ | 4/- | kJ/m² | ISO 180-1A |
| Impact strength of cantilever beam notch | |||
| 23℃ | 4/30 | kJ/m² | ISO 180-1A |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Test box with central gating, dimensions of base (107*47*1,5) mm, processing conditions: TM = 290°C, TW = 60°C |
| 3. 5000 h |
| 4. 20000 h |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |