| About |
|---|
| Without halogenes and red phosphorus a flame retarded glass fiber reinforced injection moulding grade; light in colour with outstanding mechanical and electrical properties.&& |
| Product Description | |
|---|---|
| Supplier | BASF |
| Generic | PA66 |
| Material Status | Commercial: Active |
| Features | Good Electrical Properties,Halogen free,Flame Characteristics,Low to no phosphorus content |
| Availabilitys | Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| THERMAL | Nominal value | Unit | Test method |
| Melting temperature | |||
| Injection molding/extrusion | 280 – 300 | ℃ | |
| Hot deformation temperature | |||
| 1.8 MPa | 245 | ℃ | ISO 75-1/2 |
| 0.45 MPa | 260 | ℃ | ISO 75-1/2 |
| High temperature limit, 2000h, reduced tensile strength by 50% | 130 | °C | IEC 60216 |
| High temperature limit, 5000h, reduced tensile strength by 50% | 155 | °C | IEC 60216 |
| Flammability (UL Yellow Label – see attachment) | |||
| GWFI (thickness) | 960（0.75） | °C（mm） | IEC 60695-2-12 |
| GWIT (thickness) | 722（22） | °C（mm） | IEC 60695-2-12 |
| Railway: danger levels acc, R22, and R23 | HL3（0.8-6mm） | 等级 | EN 45545-2 |
| Relative permittivity | |||
| 1 MHz | 3.8/4.6 | IEC 60250 | |
| Dissipation coefficient | |||
| 1MHz | 170/1000 | E-4 | IEC 60250 |
| Volume resistivity | 1E+16 | ohms·cm | IEC 60093 |
| Surface resistivity | 1E+15 | ohms | IEC 60093 |
| CTI, Solution A | 600 | – | IEC 60112 |
| MECHANICAL | |||
| Tensile modulus | 9500/6100 | MPa | ISO 527-1-2 |
| Tensile strain | 145/90 | % | ISO 527-1-2 |
| 3/5 | MPa | ISO 527-1/-2 | |
| Bending strength | 230/160 | MPa | ISO 527-1/-2 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 7.5/9 | kJ/m² | ISO 179/1eA |
| 23℃ | 65/65 | kJ/m² | ISO 179/1eU |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Bending modulus | 9500/6100 | MPa | ISO 527-1-2 |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 1.390 | g/cm³ | ISO 1183 |
| Viscosity value | |||
| 5% to 96% H2SO4 | 165 | cm³/g | ISO 307, 1157, 1628 |
| Water absorption rate | |||
| Saturation, 23 ℃ | 4.0 – 4.6 | % | ISO 62 |
| Moisture absorption rate | |||
| Equilibrium, 23 ℃, 50% RH | 1.10 – 1.50 | % | ISO 62 |
| Melting temperature, DSC | 260 | °C | ISO 11357-1/-3 |
| Melt Volume Rate | |||
| 275℃，5 kg | 25 | cm³/10min | ISO 1133 |
| Mold temperature, injection molding | 80-90 | °C | – |
| Shrinkage rate | |||
| MD | 0.40 | % | ISO 294-4 |
| TD | 1.20 | % | ISO 294-4 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 5000 h |
| 3. 20000 h |
| 4. Limited validity period |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |