| An easy flowing, heat aging resistant injection moulding grade for fast processing. Uses include highly stressed parts such as bearings, bearing cages, gear-wheels, coil formers and cable connectors.&& |
| Product Description | |
|---|---|
| Supplier | BASF |
| Generic | PA66 |
| Material Status | Commercial: Active |
| Features | Good heat aging resistance,Good liquidity,Quick molding cycle,Grease resistance |
| Availabilitys | Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Melt Volume Rate | |||
| 270℃，5 kg | 100 | cm³/10min | ISO 1133 |
| Density | 1.13 | g/cm³ | ISO 1183 |
| Viscosity (0.5%, 96% H2SO4) | 150 | cm³/g | ISO 307, 1157, 1628 |
| Water absorption rate | |||
| Saturation, 23 ℃ | 8.0~9.0 | % | ISO 62 |
| Equilibrium, 23 ℃, 50% RH | 2.5~3.1 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 3000 | MPa | ISO 527-1-2 |
| tensile strength | |||
| yield | 85 | MPa | ISO 527-1-2 |
| Tensile strain | |||
| yield | 4.4 | % | ISO 527-1/2 |
| fracture | 25 | % | ISO 527-1/2 |
| Tensile creep modulus (1000hs, strain<=0.5%, 23 ℃) | 700 | MPa | ISO 899-1 |
| Bending modulus | 2900 | MPa | ISO 178 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa | 75 | ℃ | ISO 75-1/2 |
| 0.45 MPa | 220 | ℃ | ISO 75-1/2 |
| Maximum operating temperature (short cycle) | 200 | ℃ | |
| Temperature index | |||
| 5000 hours, 50% loss of tensile strength | 130 | ℃ | IEC 60216 |
| 20000 hours, 50% loss of tensile strength | 109 | ℃ | IEC 60216 |
| Linear coefficient of thermal expansion | |||
| MD：23~80℃ | 70~100 | E-6/K | ISO 11359-1/-2 |
| Thermal conductivity coefficient | 0.33 | W/m/K | DIN 52612-1 |
| Specific heat capacity | 1700 | J/(kg·K) |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.60 mm | V-2 | IEC 60695 | |
| 0.80 mm | V-2 | UL 94，IEC 60695 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | NB | kJ/m² | ISO 179/1eU |
| 23℃ | 6 | kJ/m² | ISO 179/1eA |
| -30℃ | 5 | kJ/m² | ISO 179/1eA |
| Impact strength of cantilever beam notch | |||
| 23℃ | 5.5 | kJ/m² | ISO 180A |
| -30℃ | 6 | kJ/m² | ISO 180A |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Relative permittivity | |||
| 1 MHz | 3.2 | IEC 62631-2-1 | |
| Dissipation factor | |||
| 1 MHz | 250 | E-4 | IEC 62631-2-1 |
| Volume resistivity | 1×10^13 | Ohm·m | IEC 62631-3-1 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 4.0 | hr | |
| Recommended maximum moisture content | 0.15 | % | |
| Hopper temperature | 80 | °C | |
| Barrel rear temperature | 290 | °C | |
| Barrel middle temperature | 290 | °C | |
| Barrel front temperature | 290 | °C | |
| Nozzle temperature | 290 | °C | |
| Processing (melt) temperature | 280~300 | °C | |
| Mold temperature | 60~80 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Test box with central gating, dimensions of base (107*47*1,5) mm, processing conditions: TM = 290°C, TW = 60°C |
| 3. strain <= 0.5%, 23°C |
| 4. 5000 h |
| 5. 20000 h |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |