| About |
|---|
| Ultramid A3W2G6 BK20560 is a developmental 30% glass fiber reinforced, pigmented black, injection molding PA66+PA6 with high heat aging resistance. Applications Applications include automotive powertrain applications like charge air coolers.&& |
| Product Description | |
|---|---|
| Supplier | BASF |
| Generic | PA66/6 |
| Material Status | Commercial: Active |
| Features | Good heat aging resistance,Grease resistance |
| Availabilitys | North America,Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.36 | g/cm³ | |
| Melt Volume Rate | |||
| 275℃，5 kg | 20.0 | cm³/10min | |
| Water absorption rate | |||
| Saturation, 23 ℃ | 5.4 | % | |
| Equilibrium, 23 ℃, 50% RH | 1.5 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 23℃ | 9500 | MPa | |
| tensile strength | |||
| Fracture, 23 ℃ | 180 | MPa | |
| Tensile strain | |||
| Fracture, 23 ℃ | 3.5 | % | |
| Bending modulus | |||
| 23℃ | 8700 | MPa | |
| bending strength | |||
| 23℃ | 280 | MPa |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30℃ | 9.0 | kJ/m² | |
| 23℃ | 10 | kJ/m² | |
| Charpy Unnotch Impact strength | |||
| -30℃ | 70 | kJ/m² | |
| 23℃ | 90 | kJ/m² |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 230 | ℃ | |
| Melting temperature | |||
| DSC | 260 | ℃ |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.15 | % | |
| Processing (melt) temperature | 280 to 305 | °C | |
| Mold temperature | 80 to 90 | °C | |
| Injection pressure | 3.50 to 12.5 | MPa | |
| Injection speed | 快速 | ||
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |