| About |
|---|
| Ultramid A3WG6 is a 30% glass fiber reinforced and heat resistance injection molding PA66 grade for machinery components and housings of high stiffness and dimensional stability. Applications Typical applications include lamp socket housings, cooling fans, insulating profiles for aluminum window frames, water containers for automotive cooling systems.&& |
| Product Description | |
|---|---|
| Supplier | BASF |
| Generic | PA66 |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good Dimensional Stability,Grease resistance,Heat Resistance, Good |
| Availabilitys | North America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.36 | g/cm³ | ISO 1183 |
| Water absorption rate | |||
| 23℃，24hr | 5.5 | % | ISO 62 |
| 23℃，50% RH | 1.7 | % | ISO 62 |
| Melt Flow Rate | |||
| 275℃，5.0kg | 40 | g/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| 23℃ | 190 | MPa | ISO 527-2 |
| Tensile strain | |||
| Fracture, 23 ℃ | 3.0 | % | ISO 527-2 |
| Tensile modulus | |||
| 23℃ | 10000 | MPa | ISO 527-2 |
| Bending modulus | |||
| 23℃ | 8600 | MPa | ISO 178 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 250 | ℃ | ISO 75-2/Bf |
| 1.8 MPa, annealed | 250 | ℃ | ISO 75-2/Af |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volumetric resistance | 1.0E+13 | Ω.cm | IEC 60093 |
| Dielectric constant | |||
| 23℃ | 3.5 | 1 MHz | IEC 60250 |
| Dissipation factor | |||
| 23℃ | 0.014 | 100 Hz | IEC 60250 |
| 23℃ | 0.014 | 1 MHz | IEC 60250 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 0.71mm | HB | UL-94 | |
| 1.50mm | HB | UL-94 | |
| 3.00mm | HB | UL-94 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Unnotch Impact strength | |||
| 23℃ | 85 | kJ/m² | ISO 179/1eU |
| -30℃ | 70 | kJ/m² | ISO 179/1eU |
| Charpy Notched Impact Strength | |||
| 23℃ | 13 | kJ/m² | ISO 179/1eA |
| -30℃ | 11 | kJ/m² | ISO 179/1eA |
| Impact strength of cantilever beam notch | |||
| 23℃ | 12 | kJ/m² | ISO 180-1A |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 3-6 | Hr | |
| Water content | 0.12 | % | |
| Injection temperature | |||
| Rear barrel temperature | 270-290 | °C | |
| Central temperature of the barrel | 270-290 | °C | |
| Barrel front temperature | 270-290 | °C | |
| Die temperature | 280-300 | °C | |
| Mold temperature | 80-90 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |