| About |
|---|
| A glass fibre reinforced injection moulding grade with improved flame retardance. Flame retardant based on red phosphorus; giving outstanding electrical properties and very high stiffness and strength.&& |
| Product Description | |
|---|---|
| Supplier | BASF |
| Generic | PA66 |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good Electrical Properties,Flame Characteristics,Grease resistance |
| Availabilitys | Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| THERMAL | Nominal value | Unit | Test method |
| Hot deformation temperature | |||
| 1.8 MPa | 250 | ℃ | ISO 75-1/2 |
| 0.45 MPa | 250 | ℃ | ISO 75-1/2 |
| Linear coefficient of thermal expansion | |||
| Horizontal: 23~80 ° C | 40-50 | E-6/K | ISO 11359-1/-2 |
| MD：23~80℃ | 15 – 20 | E-6/K | ISO 11359-1/-2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Dielectric constant | |||
| 1MHz | 3.6 / 5 | IEC 60250 | |
| Dissipative factors | 1E13 / 1E10 | E-4 | IEC 60093 |
| Volume resistivity | /1E10 | Ohm*m | IEC 60093 |
| Surface resistivity | 600 | ohms | IEC 60112 |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melt Volume Rate | |||
| 275℃，5 kg | 25 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| TD | 0.4 | % | |
| Density | 1.600 | g/cm³ | ISO 1183 |
| Viscosity value | |||
| 0.5% in 96 % H2SO4 | 140 | cm³/g | ISO 307, 1157, 1628 |
| Water absorption rate | |||
| saturated | 3.7 – 4.3 | % | ISO 62 |
| Equilibrium, 23 ℃, 50% RH, 2.00 mm | 0.70 – 1.10 | % | ISO 62 |
| handle | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | 260 | °C | ISO 11357-1/-3 |
| Melt Temperature | 290 – 300 | °C | |
| Mold temperature | 80-90 | °C |
| Flammability | Nominal value | Unit | Test method |
|---|---|---|---|
| Burning wire flammability index | |||
| Thickness 10mm | 960 | °C | IEC 60695-2-12 |
| Extreme oxygen index | 27 | % | ISO 4589-1/-2 |
| Smoke density | 184 | EN ISO 5659-2: 2007 | |
| Smoke toxicity | 0.36 | NF X70-100-1/-2 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 16000 / 12000 | MPa | ISO 527-1-2 |
| Tensile strain | 180 / 130 | MPa | ISO 527-1-2 |
| Tensile creep modulus | |||
| * / 5400 | MPa | ISO 899-1 | |
| Bending modulus | 13000 / – | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23°C | 13 / 16 | kJ/m² | ISO 179/1eA |
| -30℃ | 11 / – | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | |||
| 23℃ | 55 / 55 | kJ/m² | ISO 179/1eA |
| -30℃ | 50 / – | kJ/m² | ISO 179/1eA |
| Impact strength of cantilever beam notch | |||
| 23℃ | 14 / 20 | kJ/m² | ISO 180-A |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Test box with central gating, dimensions of base (107*47*1,5) mm, processing conditions: TM = 320°C (unreinforced) or 330°C (reinforced), TW = 80°C |
| 3. strain <= 0.5%, 23°C |
| 4. 20000 h |
| 5. 5000 h |
| 6. 60*60*1 mm³ |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |