| About |
|---|
| Ultramid A3X2G5 BK23187 is a 25% glass fiber reinforced, pigmented black injection molding PA66 grade with improved flame retardance and enhanced long-term performance. Flame retardant based on red phosphorus; outstanding mechanical and electrical properties.&& |
| Product Description | |
|---|---|
| Supplier | BASF |
| Generic | PA66 |
| Material Status | Commercial: Active |
| Features | Flame Characteristics,Glass fiber reinforced |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.34 | g/cm³ | ISO 1183 |
| 40.0 | cm³/10min | ISO 1183 | |
| Water absorption rate | |||
| Saturation, 23 ℃ | 6.0 | % | ISO 62 |
| Equilibrium, 23 ℃, 50% RH | 1.4 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| Fracture, 23 ℃ | 125 | MPa | ISO 527-2 |
| Tensile strain | |||
| Fracture, 23 ℃ | 3.0 | % | ISO 527-2 |
| Bending modulus | |||
| 23℃ | 6900 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 7.0 | kJ/m² | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 240 | ℃ | ISO 75-2/A |
| Melting temperature | |||
| DSC | 260 | ℃ | ISO 3146 |
| Relative temperature index | |||
| Electrical performance | |||
| 0.400 mm | 110 | ℃ | UL 746 |
| 0.810 mm | 120 | ℃ | UL 746 |
| Impact mechanical performance | |||
| 1.50 mm | 120 | ℃ | UL 746 |
| 0.81 mm | 130 | ℃ | UL 746 |
| 3.00 mm | 120 | ℃ | UL 746 |
| 1.50 mm | 130 | ℃ | UL 746 |
| 0.400 mm | 115 | ℃ | UL 746 |
| 3.00 mm | 130 | ℃ | UL 746 |
| 0.810 mm | 115 | ℃ | UL 746 |
| 1.50 mm | 115 | ℃ | UL 746 |
| 3.00 mm | 115 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+13 | ohms·cm | IEC 60093 |
| Dielectric strength | 33 | kV/mm | IEC 60243-1 |
| Dissipation factor | |||
| 1 MHz | 0.020 | IEC 60250 | |
| Compared to the leakage tracing index | 550 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 0.81 mm | V-0 | UL 94 | |
| 1.50 mm | V-0 | UL 94 | |
| 3.00 mm | V-0 | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.050 | % | |
| Processing (melt) temperature | 285 to 300 | °C | |
| Mold temperature | 80 to 90 | °C | |
| Injection pressure | 3.50 to 12.5 | MPa | |
| Injection speed | 快速 | ||
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |