| About |
|---|
| Product Description | |
|---|---|
| Supplier | BASF |
| Generic | PA66 |
| Material Status | Commercial: Negative |
| Features | Good Electrical Properties,V-0,Grease resistance,Flame Characteristics |
| Availabilitys | Europe,Asia Pacific,North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.38 | g/cm³ | ISO 1183 |
| Water absorption rate | |||
| 23 ℃, in water | 0.75 | % | ISO 62 |
| Equilibrium, 23 ℃, 50% RH | 2.1 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 23℃ | 9400 | MPa | ISO 527-2 |
| Tensile stress | ISO 527-2 | ||
| fracture | 150 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 2.5 | % | ASTM D638 |
| Bending modulus | 8500 | MPa | ISO 178 |
| bending strength | 255 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30℃ | 7 | kJ/m² | ISO 179/1eA |
| 23℃ | 8 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | |||
| -30℃ | 50 | kJ/m² | ISO 179/1eU |
| 23℃ | 55 | kJ/m² | ISO 179/1eU |
| Impact strength of cantilever beam notch | |||
| 23℃ | 8 | KJ/m² | ISO 180/1A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 244 | ℃ | ISO 75-2/A |
| Melting temperature | |||
| DSC | 263 | ℃ | ISO 3146 |
| ELECTRICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+13 | ohm | IEC 62631-3-2 |
| Dielectric strength | |||
| 0.8 mm | 30 | kV/mm | IEC 60243-1 |
| Dielectric constant | |||
| 100 Hz | 3.4 | IEC 62631-2-1 | |
| Dissipation factor | |||
| 100 Hz | 2.0E-6 | IEC 62631-2-1 | |
| Compared to the leakage tracing index | 400 | V | IEC 60112 |
| Volume resistivity | 1.0E+13 | ohm·cm | IEC 62631-3-1 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 0.80 mm | V-0 | UL 94 | |
| 1.50 mm | V-0 | UL 94 | |
| 3.00 mm | V-0 | UL 94 | |
| Glowing wire flammability index | |||
| 0.80 mm | 960 | ℃ | IEC 60695-2-12 |
| 1.60 mm | 960 | ℃ | IEC 60695-2-12 |
| 3.20 mm | 960 | ℃ | IEC 60695-2-12 |
| Igniting temperature of the hot wire | |||
| 1.60 mm | 725 | ℃ | IEC 60695-2-13 |
| Extreme oxygen index | 31 | % | ISO 4589-1/-2 |
| Process Conditions | |||
|---|---|---|---|
| Injection | Nominal value | Unit | Test method |
| drying temperature | 80 | °C | null |
| Suggested maximum moisture content | 0.2 | % | null |
| Temperature of the rear section of the barrel | 265 – 275 | °C | null |
| Temperature in the middle section of the barrel | 270 – 280 | °C | null |
| Temperature of the front section of the material barrel | 280 – 290 | °C | null |
| Mold temperature | 60 – 90 | °C | null |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |