| Ultramid A3XZG5 is an impact-modified, 25% glass fiber reinforced injection molding PA66 grade with improved flame retardance. Flame retardant based on red phosphorus. Applications Typical applications include components with high stiffness, dimensional stability and enhanced impact strength such as electrical switches.&& |
| Product Description | |
|---|---|
| Supplier | BASF |
| Generic | PA66 |
| Material Status | Commercial: Active |
| Features | Good Rigidity,High impact resistance,Good Dimensional Stability,Flame Characteristics,Grease resistance,HB,V-0 |
| Availabilitys | North America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.32 | g/cm³ | ISO 1183 |
| Water absorption rate | |||
| Saturation, 23 ℃ | 5.0 | % | ISO 62 |
| Equilibrium, 23 ℃, 50% RH | 1.2 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 23℃ | 6500 | MPa | ISO 527-2 |
| tensile strength | |||
| Fracture, 23 ℃ | 105 | MPa | ISO 527-2 |
| Tensile strain | |||
| Fracture, 23 ℃ | 6.0 | % | ISO 527-2 |
| Bending modulus | |||
| 23℃ | 5500 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 25 | kJ/m² | ISO 179 |
| Charpy Unnotch Impact strength | |||
| 23℃ | 90 | kJ/m² | ISO 179 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 240 | ℃ | ISO 75-2/A |
| 0.45 MPa, unannealed | 250 | ℃ | ISO 75-2/B |
| Melting temperature | |||
| DSC | 260 | ℃ | ISO 3146 |
| 0.75 mm | 120 | ℃ | UL 746 |
| 1.5 mm | 120 | ℃ | UL 746 |
| 3.0 mm | 120 | ℃ | UL 746 |
| Relative temperature index | |||
| Electrical performance | UL 746 | ||
| Strength mechanical performance | UL 746 | ||
| Impact mechanical performance | UL 746 | ||
| 0.75 mm | 115 | ℃ | UL 746 |
| 1.5 mm | 115 | ℃ | UL 746 |
| 3.0 mm | 115 | ℃ | UL 746 |
| 1.5 mm | 130 | ℃ | UL 746 |
| 3.0 mm | 130 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Dielectric constant | |||
| 1 MHz | 3.80 | IEC 60250 | |
| Dissipation factor | |||
| 1 MHz | 0.020 | IEC 60250 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 0.75 mm | HB | UL 94 | |
| 1.50 mm | V-0 | UL 94 | |
| 3.00 mm | V-0 5VA | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.050 | % | |
| Barrel rear temperature | 285 to 300 | °C | |
| Barrel middle temperature | 285 to 300 | °C | |
| Barrel front temperature | 285 to 300 | °C | |
| Mold temperature | 80 to 90 | °C | |
| Injection pressure | 3.50 to 12.5 | MPa | |
| Injection speed | Fast | ||
| Notes |
|---|
| 1. Thickness >= 1mm |
| 2. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |