| About |
|---|
| A high heat aging resistant, medium viscosity injection moulding grade for highly stressed parts such as bearing cages, gear-wheels, coil formers and cable connectors.&& |
| Product Description | |
|---|---|
| Supplier | BASF |
| Generic | PA66 |
| Material Status | Commercial: Active |
| Features | Grease resistance,Good heat aging resistance |
| Availabilitys | Europe,Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| handle | Nominal value | Unit | Test method |
| Melting temperature | 260 | °C | ISO 11357-1/-3 |
| Melting temperature | 280-300 | ℃ | |
| Mold temperature | 60-80 | °C | – |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 1.6 mm | V-2 | – | IEC 60695-11-10 |
| >= 1mm | – | + | FMVSS 302 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 3100/1200 | MPa | ISO 527-1-2 |
| Tensile stress | 85/50 | MPa | ISO 527-1/-2 |
| yield | 4.2/20 | % | ISO 527-1/2 |
| Tensile fracture | 25/>50 | % | ISO 527-1/-2 |
| Tensile modulus | |||
| 1000h, strain<=0.5%, 23 ℃ | */700 | MPa | ISO 899-1 |
| Bending modulus | 3000/- | MPa | ISO 178 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa | 75 | ℃ | ISO 75-1/2 |
| 0.45 MPa | 250 | ℃ | ISO 75-1/2 |
| Maximum operating temperature | |||
| Short cycle operation | 200 | °C | – |
| Temperature index 5000 hours after 50% loss of tensile strength | 138 | °C | IEC 60216 |
| Temperature index after a 50% loss in tensile strength for 20000 hours | 118 | °C | IEC 60216 |
| Linear thermal expansion coefficient | |||
| MD 23-80°C | 70-100 | E-6/K | ISO 11359-1/-2 |
| Thermal conductivity | 0.33 | w(mk) | DIM52612-1 |
| Specific heat capacity | 1700 | J/(kg*K) | – |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| 1 MHz | 3.2/5 | IEC 60250 | |
| 1 MHz | 250/2000 | E-4 | IEC 60250 |
| Surface resistivity | 1E+13 | ohms | IEC 60093 |
| Volume resistivity | */1E10 | Ohm | IEC 60093 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 5.7/25 | kJ/m² | ISO 179/1eU |
| 23℃ | N/N | kJ/m² | ISO 179/1eU |
| 23℃ | 5.5/N | kJ/m² | ISO 180-A |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melt Volume Rate | |||
| 275℃，5 kg | 40 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| Restricted 3 | 0.9 | % | |
| Density | 1.130 | g/cm³ | ISO 1183 |
| Viscosity value | 190 | g/cm³ | ISO 307, 1157, 1628 |
| Water absorption rate | |||
| saturated | 8.0-9.0 | % | ISO 62 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Test box with central gating, dimensions of base (107*47*1,5) mm, processing conditions: TM = 290°C, TW = 60°C |
| 3. strain <= 0.5%, 23°C |
| 4. 5000 h |
| 5. 20000 h |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |