| Product Description | |
|---|---|
| Supplier | BASF |
| Generic | PA66 |
| Material Status | Commercial: Active |
| Features | Good heat aging resistance,Grease resistance,Medium Viscosity |
| Availabilitys | Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Melt Volume Rate | |||
| 275℃，5 kg | 40 | cm³/10min | ISO 1133 |
| Density | 1.13 | g/cm³ | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 3200 | MPa | ISO 527 |
| tensile strength | |||
| yield | 85 | MPa | ISO 527 |
| Tensile strain | |||
| yield | 4.2 | % | ISO 527 |
| fracture | ＞50 | % | ISO 527 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Unnotch Impact strength | |||
| 23℃ | 未断裂 | kJ/m² | ISO 179/1eU |
| Charpy Notched Impact Strength | |||
| 23℃ | 5.7 | kJ/m² | ISO 179/1eA |
| -30℃ | 5 | kJ/m² | ISO 179/1eA |
| Impact strength of cantilever beam notch | |||
| 23℃ | 6 | kJ/m² | ISO 180-1eA |
| -30℃ | 7 | kJ/m² | ISO 180-1eA |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| melting point | 260 | °C | ISO 11357-1/-3 |
| Hot deformation temperature | |||
| 1.8 Mpa | 75 | ℃ | ISO 75-1/2 |
| 0.45 MPa | 220 | ℃ | ISO 75-1/2 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | V-2 | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| Injection | Nominal value | Unit | Test method |
| drying temperature | 80 | °C | |
| Drying time | 4.0 | hr | |
| Recommended maximum moisture content | 0.15 | % | |
| Hopper temperature | 80 | °C | |
| Temperature at the rear of the barrel | 290 | °C | |
| Temperature in the middle of the barrel | 290 | °C | |
| Front temperature of material barrel | 290 | °C | |
| Nozzle temperature | 290 | °C | |
| Processing (melt) temperature | 280 to 300 | °C | |
| Mold temperature | 60 to 80 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |