| About |
|---|
| Product Description | |
|---|---|
| Supplier | BASF |
| Generic | PA 6T/66 |
| Material Status | Commercial: Negative |
| Features | Solvent resistance,Heat Resistance, Good |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1390 | kg/m³ | ISO 1183 |
| Water absorption rate | |||
| Balance, 23 ° C, 50% RH | 1.32 | % | ISO 62 |
| Viscosity value | |||
| 0.5% in 96 % H2SO4 | 125 | cm³/g | ISO 307, 1157, 1628 |
| Mold shrinkage rate | |||
| TD | 0.52 | % | ISO 294-4 |
| MD | 1.13 | % | ISO 294-4 |
| Melt Volume Rate | |||
| 320 °C，5 kg | 2 | cm³/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 23℃ | 10200 | MPa | ISO 527-1/-2 |
| Tensile stress | |||
| Fracture, 23 ℃ | 188 | MPa | ISO 527-1/-2 |
| Tensile strain | |||
| Fracture, 23 ℃ | 2.8 | % | ISO 527-1/-2 |
| Bending modulus | |||
| 23℃ | 9200 | MPa | ISO 178 |
| bending strength | 340 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Unnotch Impact strength | |||
| -30℃ | 55 | kJ/m² | ISO 179/1eU |
| 23℃ | 86 | kJ/m² | ISO 179/1eU |
| Charpy Notched Impact Strength | |||
| -30℃ | 7.3 | kJ/m² | ISO 179/1eA |
| 23℃ | 8.7 | kJ/m² | ISO 179/1eA |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.80 MPa | 280 | ℃ | ISO 75-1/-2 |
| 0.45 MPa | 280 | ℃ | ISO 75-1/-2 |
| Process Conditions | |||
|---|---|---|---|
| Injection | Nominal value | Unit | Test method |
| Mold temperature | 120 – 160 | °C | |
| Melt Temperature | 320 – 340 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |