| About |
|---|
| Glass fibre reinforced injection moulding grade e.g. for internal gas pressure applications such as steering column switch, automobile mirror housings and wheels of mountain bikes.&& |
| Product Description | |
|---|---|
| Supplier | BASF |
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | Grease resistance |
| Availabilitys | North America,Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.24 | g/cm³ | ISO 1183 |
| Melt Volume Rate | |||
| 275℃，5 kg | 45.0 | cm³/10min | ISO 1133 |
| Water absorption rate | |||
| Saturation, 23 ℃ | 8.0 | % | ISO 62 |
| Equilibrium, 23 ℃, 50% RH | 2.6 | % | ISO 62 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 5.9 | kJ/m² | ISO 179 |
| Charpy Unnotch Impact strength | |||
| 23℃ | 47 | kJ/m² | ISO 179 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 187 | ℃ | ISO 75-2/A |
| 0.45 MPa, unannealed | 214 | ℃ | ISO 75-2/B |
| Melting temperature | |||
| DSC | 220 | ℃ | ISO 3146 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Compared to the leakage tracing index | 500 | V | IEC 60112 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 23℃ | 6100 | MPa | ISO 527-2 |
| tensile strength | ISO 527-2 | ||
| Fracture, -40 ℃ | 156 | MPa | ISO 527-2 |
| Fracture, 23 ℃ | 126 | MPa | ISO 527-2 |
| Tensile strain | ISO 527-2 | ||
| Fracture, -40 ℃ | 3.5 | % | ISO 527-2 |
| Fracture, 23 ℃ | 2.9 | % | ISO 527-2 |
| bending strength | |||
| 23℃ | 189 | MPa | ISO 178 |
| Ball hardness | 181 | MPa | ISO 2039-1 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.15 | % | |
| Processing (melt) temperature | 250 to 290 | °C | |
| Mold temperature | 80 to 95 | °C | |
| Injection pressure | 3.50 to 12.5 | MPa | |
| Injection speed | Fast | ||
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Test box with central gating, dimensions of base (107*47*1,5) mm, processing condition: TM = 280°C, TW = 80°C |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |