| About |
|---|
| Glass fibre reinforced injection moulding grade for industrial articles and electrical insulating parts.&& |
| Product Description | |
|---|---|
| Supplier | BASF |
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | Grease resistance |
| Availabilitys | Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.32 | g/cm³ | ISO 1183 |
| bulk density | 140 | cm³/g | ISO 307 |
| Water absorption rate | |||
| 23℃ | 6.8-7.4 | % | ISO 62 |
| 23℃/50%r.h. | 2.1-2.5 | % | ISO 62 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.6 mm | HB | IEC 60695-11-10 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 8000 | MPa | ISO 527-2 |
| Process Conditions | |||
|---|---|---|---|
| Injection | Nominal value | Unit | Test method |
| drying temperature | 80 | °C | |
| Drying time | 4.0 | hr | |
| Recommended maximum moisture content | 0.15 | % | |
| Hopper temperature | 80 | °C | |
| Temperature at the rear of the barrel | 260 | °C | |
| Temperature in the middle of the barrel | 270 | °C | |
| Front temperature of material barrel | 280 | °C | |
| Nozzle temperature | 280 | °C | |
| Processing (melt) temperature | 270 to 290 | °C | |
| Mold temperature | 80 to 90 | °C | |
| Residence Time | < 10.0 | min | |
| Screw Speed | < 300 | mm/sec | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Test box with central gating, dimensions of base (107*47*1,5) mm, processing conditions: TM = 280°C, TW = 80°C |
| 3. strain <= 0.5%, 23°C |
| 4. 5000 h |
| 5. 20000 h |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |