| About |
|---|
| Glass fibre-reinforced injection moulding grade, with excellent surface quality especially suitable for the production of visible parts with very high stiffness. Optimum surface quality is generally obtained at a very high injection speed.&& |
| Product Description | |
|---|---|
| Supplier | BASF |
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good surface appearance,Grease resistance |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.57 | g/cm³ | |
| Apparent density | 0.70 | g/cm³ | |
| Melt Volume Rate | |||
| 275℃，5 kg | 12.0 | cm³/10min | |
| Viscosity number | |||
| 96% H2SO4 | 135 | cm³/g | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 16500 | MPa | |
| tensile strength | |||
| fracture | 235 | MPa | |
| Tensile strain | |||
| fracture | 3.0 | % | |
| Bending modulus | 13500 | MPa | |
| bending strength | 340 | MPa |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30℃ | 16 | kJ/m² | |
| 23℃ | 20 | kJ/m² | |
| Charpy Unnotch Impact strength | |||
| -30℃ | 85 | kJ/m² | |
| 23℃ | 95 | kJ/m² |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 215 | ℃ | |
| 1.8 MPa, unannealed | 200 | ℃ |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Polymer Abbreviation | PA6-GF50 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 4.0 | hr | |
| Recommended maximum moisture content | 0.15 | % | |
| Hopper temperature | 80 | °C | |
| Barrel rear temperature | 290 | °C | |
| Barrel middle temperature | 290 | °C | |
| Barrel front temperature | 290 | °C | |
| Nozzle temperature | 290 | °C | |
| Processing (melt) temperature | 280 to 300 | °C | |
| Mold temperature | 80 to 110 | °C | |
| Residence Time | < 10.0 | min | |
| Screw Speed | < 18 | m/min | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |