| About |
|---|
| Ultramid B3K is an easy flowing, stabilized PA6 product for fast processing. Applications Typical applications include technical parts with wall thicknesses greater than 2 mm.&& |
| Product Description | |
|---|---|
| Supplier | BASF |
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | Good liquidity,Grease resistance,HB,V-2 |
| Availabilitys | North America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.13 | g/cm³ | ASTM D792 |
| Density | 1.13 | g/cm³ | ISO 1183 |
| Melt Volume Rate | |||
| 275℃，5 kg | 160 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| MD：3.2 mm | 1.0 | % | |
| Water absorption rate | |||
| Saturation, 23 ℃ | 9.5 | % | ISO 62 |
| saturated | 9.5 | % | ASTM D570 |
| Equilibrium, 23 ℃, 50% RH | 3.0 | % | ISO 62 |
| Balance, 50% RH | 3.0 | % | ASTM D570 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 23℃ | 3000 | MPa | ISO 527-2 |
| tensile strength | |||
| Fracture, 23 ℃ | 80.0 | MPa | ISO 527-2 |
| Yield, 23 ℃ | 90.0 | MPa | ASTM D638 |
| Yield, 23 ℃ | 85.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| Fracture, 23 ℃ | 20 | % | ASTM D638 |
| Yield, 23 ℃ | 3.7 | % | ISO 527-2 |
| Yield, 23 ℃ | 3.7 | % | ASTM D638 |
| Nominal tensile fracture strain | |||
| 23℃ | 20 | % | ISO 527-2 |
| Bending modulus | |||
| 23℃ | 2600 | MPa | ISO 178 |
| 23℃ | 2600 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30℃ | 4.0 | kJ/m² | ISO 179 |
| 23℃ | 5.5 | kJ/m² | ISO 179 |
| Charpy Unnotch Impact strength | ISO 179 | ||
| -30℃ | 100 | kJ/m² | ISO 179 |
| 23℃ | No Break | ISO 179 | |
| Impact strength of cantilever beam notch | |||
| 23℃ | 5.6 | kJ/m² | ISO 180 |
| 23℃ | 75 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 65.0 | ℃ | ISO 75-2/A |
| 1.8 MPa, unannealed | 65.0 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed | 160 | ℃ | ASTM D648 |
| Melting peak temperature | 220 | ℃ | ASTM D3418 |
| Melting temperature | |||
| DSC | 220 | ℃ | ISO 3146 |
| Linear coefficient of thermal expansion | |||
| MD | 8.5E-5 | 1/℃ | |
| MD | 4.0E-5 | 1/℃ | ASTM E831 |
| 0.71 mm | 130 | ℃ | UL 746 |
| 1.5 mm | 130 | ℃ | UL 746 |
| 3.0 mm | 130 | ℃ | UL 746 |
| 6.0 mm | 130 | ℃ | UL 746 |
| Relative temperature index | |||
| Electrical performance | UL 746 | ||
| Strength mechanical performance | UL 746 | ||
| Impact mechanical performance | UL 746 | ||
| 1.5 mm | 75.0 | ℃ | UL 746 |
| 3.0 mm | 75.0 | ℃ | UL 746 |
| 6.0 mm | 75.0 | ℃ | UL 746 |
| 1.5 mm | 115 | ℃ | UL 746 |
| 3.0 mm | 115 | ℃ | UL 746 |
| 6.0 mm | 115 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+13 | ohms·cm | IEC 60093 |
| 1.50 mm | 1.0E+13 | ohms·cm | ASTM D257 |
| Dielectric constant | IEC 60250 | ||
| 100 Hz | 4.00 | IEC 60250 | |
| 1 MHz | 3.50 | IEC 60250 | |
| Dissipation factor | IEC 60250 | ||
| 100 Hz | 0.010 | IEC 60250 | |
| 1 MHz | 0.023 | IEC 60250 | |
| Compared to the leakage tracing index | 600 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 1.50 mm | HB | UL 94 | |
| 3.00 mm | V-2 | UL 94 | |
| 6.00 mm | V-2 | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.15 | % | |
| Processing (melt) temperature | 240 to 285 | °C | |
| Mold temperature | 65 to 80 | °C | |
| Injection pressure | 3.50 to 12.5 | MPa | |
| Injection speed | Fast | ||
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |