| Ultramid B3M6 BK60564 is a 30% mineral reinforced, pigmented black injection molding PA6 grade for industrial items requiring high impact strength and very high dimensional stability, excellent laser markability. Applications Typical applications include industrial items.&& |
| Product Description | |
|---|---|
| Supplier | BASF |
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | High impact resistance,Good Dimensional Stability,Grease resistance,Laser engraving |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.36 | g/cm³ | ASTM D792 |
| Density | 1.36 | g/cm³ | ISO 1183 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.90 | % | |
| Water absorption rate | |||
| Saturation, 23 ℃ | 6.2 | % | ISO 62 |
| saturated | 6.2 | % | ASTM D570 |
| Equilibrium, 23 ℃, 50% RH | 2.4 | % | ISO 62 |
| Balance, 50% RH | 2.4 | % | ASTM D570 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 23℃ | 3700 | MPa | ISO 527-2 |
| tensile strength | |||
| Fracture, 23 ℃ | 85.0 | MPa | ASTM D638 |
| Fracture, 23 ℃ | 85.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| Fracture, 23 ℃ | 4.9 | % | ISO 527-2 |
| Fracture, 23 ℃ | 4.9 | % | ASTM D638 |
| Bending modulus | |||
| 23℃ | 3270 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 5.6 | kJ/m² | ISO 179 |
| Impact strength of cantilever beam notch | ASTM D256 | ||
| -40℃ | 45 | J/m | ASTM D256 |
| 23℃ | 64 | J/m | ASTM D256 |
| Impact strength of cantilever beam notch | ISO 180 | ||
| -40℃ | 4.0 | kJ/m² | ISO 180 |
| 23℃ | 5.5 | kJ/m² | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 120 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 70.0 | ℃ | ISO 75-2/A |
| 0.45 MPa, unannealed | 160 | ℃ | ISO 75-2/B |
| 0.45 MPa, unannealed | 195 | ℃ | ASTM D648 |
| Melting peak temperature | 220 | ℃ | ASTM D3418 |
| Melting temperature | |||
| DSC | 220 | ℃ | ISO 3146 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| 1.50 mm | > 1.0E+15 | ohms·cm | ASTM D257 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |